Abstract:With increasing the possibilities of tribological applications for Al2O3 ceramic, much more attentions have been paid to researches on the tribological characteristics of Al2O3, such as compositions, microstructures, environments and other tribo-parameters. The effect of surface roughness of self-mated Al2O3 on friction and wear has been investigated at the present paper by varying the roughness parameters of samples under the conditions of reciprocating contact of cylinder-on-plate geometry lubricated by isooctane. In the tribotests, the roughness of plate samples were varied and they were ground by diamond grinding wheels. The surface of cylinders was, however, kept as delivered conditions. A dry air tribotest was also carried out to be as a reference test compared to lubricated tests. It has been found in this investigation that the increase of surface roughness results in high linear wear and friction coefficient of cylinder-plate tribopairs. It was observed that there exists a critical roughness about R-vk 1.89. High friction coefficient and linear wear will be got above this critical roughness. If the roughness of plate is below this critical value, friction coefficient and linear wear will be quite small after the test. It is also found by the SEM examinations of worn Surfaces that a thick third body layer is formed during the test with higher surface roughness of plates. The thin and compacted third body layer is formed with lower roughness of plates. Therefore, a carefully finished ceramic surface is extremely important to improve the tribological behaviours for engineering applications. It is interesting that the linear wear of as delivered cylinder-plate sample pairs is quickly levelled off in the dry air conditions even though their friction coefficient still keeps around 0.7. It can be concluded from this test that lubricant may have a negative effect on tribological behaviors.

Tribological mechanisms of slurry abrasive wear

Waviness Affects Friction and Abrasive Wear

Mechanisms of abrasive wear in lubricated contacts

Wear Rate, Frictional Temperature, and Energy Consumption of Steel 52100 with Different Microstructures During Sliding

Formation and wear mechanism of tribo-oxides and the regime of oxidational wear of steel

Effect of surface polishing on the tribological performance of hard coatings under lubricated three-body abrasive conditions

Wear Mechanism and Three-phase Synergistic Effect of Self-mated SiC/Si/Graphite Composites in Unlubricated Sliding

Tribological Behavior of Various Plasma-Sprayed Ceramic Coatings

Tribological mechanism of micro/meso/macroscopic textured surfaces under different normal forces, relative velocities, and sliding directions

Studies of Simultaneous Friction and Corrosive Processes in the Presence of Abrasive Particles

Effect of the Micro-Structure Evolution of Friction Layer on the Sliding Tribology Behavior of TiAl-10 Wt.% Ag at 16 N-0.5 M/s

Effect Of Surface Roughness And Wear In Lubricated Of Self-Mated Alumina On Friction Reciprocating Sliding Contact

Wear Behavior of Medium Carbon Steel with Biomimetic Surface under Starved Lubricated Conditions

Subsurface Dynamic Deformation and Nano-structural Evolution in 40cr Steel under Dry Sliding Wear

Wear Behavior Of Steel 1080 With Different Microstructures During Dry Sliding

Ti6Al4V interacting with Al 2 O 3 under Ambient and Vacuum Conditions: Effect of Plastic Deformation and Tribo-Chemical Reactions on Wear Mechanisms

Tribological Properties of Al2O3/Graphite-Al2O3 Laminated Composites under Water Lubrication Conditions

Grease-lubricated Tribological Behaviour of Nitrided Layer on 2cr13 Steel in Vacuum

The Mechanism of Tribological Wear of Thermoplastic Materials

Wear characteristics and sustainability of WS2 solid lubricant deposited layer on Al 6061-T6 substrate under the dry sliding conditions

Tribological behavior of carbon steel 45 and brass H90 in dry sliding on bearing steel GCr15 in the sand-dust environment