Abstract:<p>Two flux thimble tubes (FTT) made of 15% cold-worked 316 stainless steel (SS) were harvested from Ringhals Pressurized Water Reactor (PWR) Unit 2, with peak damages of 76 and 100 displacements per atom (dpa) after 29 and 34 years' service, respectively. Specimens sectioned from parent tubes were comprehensively characterized with nominal damage levels of ∼0, ∼41, ∼74, 76, and 100 dpa at a nominal temperature range of 285-323 °C. Both FTTs contained helium and hydrogen gases as transmutation products. The helium follows a production rate of ∼9.8 appm/dpa, while environmental factors complicate hydrogen production obscuring an exact H/dpa ratio. Irradiation-induced dislocation loops, nano-cavities, solute clusters, and microsegregation were all observed. The dislocation loops and nano-cavities indicated saturation at 41 dpa. The solute clusters continued to evolve with Ni-Si clusters formed at 41 dpa, and Ni-Si-Mn-P clusters formed at 74 and 100 dpa, but neither clusters exhibited distinct diffraction patterns at any damage levels. Solute clusters were observed to frequently be co-located with dislocation loops, but fully decorated loops were rarely detected. Significant radiation-induced segregation (RIS) was observed around grain boundaries at all damage levels. The modified inverse Kirkendall (MIK) model captured the RIS behavior of major elements. Large cavities within or around an Mn-S rich region were observed for the first time. Through all the damage levels, void swelling is always below 0.05%, making significant dimensional change unlikely in core internals when used at similar conditions. Meanwhile, the role of overwhelming nanocavities, presumably helium bubbles, should be considered in other potential degradation mechanisms, including irradiation-assisted stress corrosion cracking, embrittlement, and loss of fracture toughness, which remain the concerns for extended operation of nuclear power plants.</p>

Examination of Variable Frequency Drive Transformer Copper Cooling Line Failures from Nuclear Power Plants

Failure Analysis on Unexpected Fracture of the Hydraulic Expansion Mandrel for Tube to Tubesheet Expanding in the Steam Generator of Nuclear Power Plant

Failure Analysis on Premature Fracture of Boric Acid Recycle Pump Shaft in 1000 MW Nuclear Power Plant

Failure Analysis of CRDINiCr Butterfly Valves for Nuclear Power Plant Applications

Causes of transformer failures and diagnostic methods – A review

Failure Analysis on Speed Reducer Shaft of Sluice Gate in Nuclear Power Plant

Failure Analysis of Leakage on Titanium Tubes Within Heat Exchangers in a Nuclear Power Plant. Part II: Mechanical Degradation

On the role of intergranular nanocavities in long-term stress corrosion cracking of Alloy 690

Failure Analysis on Abnormal Bursting of Heat Transfer Tubes in Spiral-Wound Heat Exchanger for Nuclear Power Plant

Failure analysis of reheater tubes in a 350 MW supercritical circulating fluidized bed boiler

Failure analysis on abnormal leakage of radiator for high-speed train transformer

Failure analysis of titanium heater tubes and stainless steel heat exchanger weld joints in nitric acid loop

A Preliminary Study on the Formation Mechanism of Microcracks in Dry-type Air-core Shunt Reactors

Failure Analysis on Premature Fracture of Anchor Bolts in Seawater Booster Pump of Nuclear Power Plant

Failure analysis on fracture causes of stainless-steel studs in seawater system of nuclear power plants

Failure analysis of leaking firefighting pipeline used in nuclear power plant: Corrosion development process and key influence factors

Failure Analysis of Compressor IGV in 9F Gas Turbine Generator Unit

Microstructural characterization of cold-worked 316 stainless steel flux thimble tubes irradiated up to 100 dpa in a commercial Pressurized Water Reactor

Failure Analysis on Abnormal Leakage Between Tubes and Tubesheet of Spiral-Wound Heat Exchanger for Nuclear Power Plant

Failure Analysis of Stainless Steel Heat Exchanger Tubes in a Petrochemical Plant