Abstract:Polyvinylidene fluoride (PVDF)–perfluorosulfonic acid (PFSA) blend hollow fiber ultrafiltration (UF) membranes were prepared by wet-spinning method using pure water as an external coagulation solution. Coagulation kinetics of PVDF–PFSA–DMAc system was measured by light transmittance experiment. Using PEG10000 (Mw=10,000), lysozyme (Mw=14,400), PEG20000 (Mw=20,000) and BSA (Mw=67,000), the separation performances of PVDF–PFSA blend hollow fiber UF membranes were obtained. Based on the experimental results, the delayed demixing process was observed for the dope solution M-1 without PFSA-H while the instantaneous demixing process was observed for the others with PFSA-H in the dope solutions M-2 to M-6. The precipitation rate increased with the increment of the PFSA-H concentration in PVDF–PFSA dope solution. The bore fluid solution with 95:5 DMAc:H2O resulted in single finger-like voids for PVDF–PFSA-H UF membrane. The pure water permeation flux of PVDF–PFSA-H UF membranes firstly increased from <0.1×10−5 to 119.1×10−5Lm−2h−1Pa−1 (<0.1 to 119.1Lm−2h−1bar−1) for M-1 to M-4(1) and 137×10−5Lm−2h−1Pa−1 (137Lm−2h−1bar−1) for M-4(2), and decreased from 119.1×10−5 to 79×10−5Lm−2h−1Pa−1 (119.1 to 79Lm−2h−1bar−1) for M-4(1), M-5 and M-6 as the PFSA-H concentration changed from 0% to 5% and total PVDF–PFSA-H concentration was 20wt.%. The molecular weight cut-off (MWCO) of PVDF–PFSA blend hollow fiber UF membranes spun from 20wt.% PVDF–PFSA-H concentration with 3–5wt.% PFSA-H was about 20,000 while that spun from 22wt.% PVDF–PFSA-H or PVDF–PFSA-Na concentration with 5wt.% PFSA-H or PFSA-Na was about 10,000. As the WPFSA-H/WPVDF increases from 2/18 to 5/15 for M-3–M-6, JBSA/Jw increases from 0.53 to 0.79. The anti-fouling property of PVDF–PFSA-H blend UF membrane is superior to PVDF–PFSA-Na blend membrane. Based on FTIR spectra, PFSA-H existed in PVDF–PFSA blend hollow fiber UF membranes. There is no obvious variation of the intensity of the characteristic peak at 983cm−1 assigned to C–O–C group of PFSA-H molecules. This also illustrated that PVDF–PFSA-H blend hollow fiber UF membranes were stable.

Structure-performance-fouling studies of polysulfone microfiltration hollow fibre membranes

Structure formation and characterization of PVDF hollow fiber membranes by melt-spinning and stretching method

Preparation and Performance of Polyethersulfone Hollow-Fiber Membrane

Fabrication of Polysulfone-Based Microfiltration Membranes and Their Performance Analysis

A novel polysulfate hollow fiber membrane with antifouling property for ultrafiltration application

Morphology and Performance of Polyvinylidene Fluoride/Perfluorosulphonic Acid Hollow Fibre Ultrafiltration Blend Membranes

Characterization of PVDF–PFSA hollow fiber UF blend membrane with low-molecular weight cut-off

Novel polysulfone hybrid ultrafiltration membrane prepared with TiO2-g-HEMA and its antifouling characteristics

Zwitterionic Polysulfone Copolymer/Polysulfone Blended Ultrafiltration Membranes with Excellent Thermostability and Antifouling Properties

Polymer Concentration and Solvent Variation Correlation with the Morphology and Water Filtration Analysis of Polyether Sulfone Microfiltration Membrane

Preparation Of Micro-Porous Polyethersulphone Hollow Fibre Membranes Using Non-Solvent Vapour-Induced Phase Separation

Preparation and characterization of PVDF–PFSA blend hollow fiber UF membrane

Study on the Preparation of Hollow Fiber Ultra-filtration Membrane of PSF-SPES Blend

Fabrication of polysulfone ultrafiltration membranes of a density gradient cross section with good anti-pressure stability and relatively high water flux

Preparation of Polysulfone Composite Membrance and Study on Its Air Filtration Performance

Zwitterionic Analog Structured Ultrafiltration Membranes for High Permeate Flux and Improved Anti-Fouling Performance

Improved Antifouling Properties of Poly(Ether Sulfone) Membrane by Incorporating the Amphiphilic Comb Copolymer with Mixed Poly(Ethylene Glycol) and Poly(Dimethylsiloxane) Brushes

Study on the preparation of PDMS/PSF hollow fiber composite pervaporation membrane

Comprehensive Analysis of Spinel-Type Mixed Metal Oxide-Functionalized Polysulfone Membranes toward Fouling Resistance and Dye and Natural Organic Matter Removal

Preparation of polysulfone/sulfonated polysulfone-SiO 2 nanofiltration membrane and its performance characterization

Effect of Membrane Pore Morphology on Microfiltration Organic Fouling: PTFE/PVDF Blend Membranes Compared with PVDF Membranes