Insight into fouling behavior of poly(vinylidene fluoride) (PVDF) hollow fiber membranes caused by dextran with different pore size distributions

Kailiang Zeng,Jie Zhou,Zhaoliang Cui,Yue Zhou,Chuan Shi,Xiaozu Wang,Liyue Zhou,Xiaobin Ding,Zhaohui Wang,Enrico Drioli

DOI: https://doi.org/10.1016/j.cjche.2017.04.008

IF: 3.8

2018-01-01

Chinese Journal of Chemical Engineering

Abstract:Membrane fouling is the key problem that occurs in membrane process for water treatment. However, how membrane microstructure influences the fouling behavior is still not clear. In this study, fouling behavior caused by dextran was deeply and systematically investigated by employing four poly(vinylidene fluoride) (PVDF) membranes with different pore sizes, ranging from 24 to 94nm. The extent of fouling by dextran was accurately characterized by pore reduction, flux decline, and the change of critical flux. The result shows that membrane with the smallest pore size of 24nm experienced the smallest fouling rate and the lowest fouling extent. As the membrane pore size increased, the critical flux ranges were 105–114, 63–73, 38–44 and 34–43L·m−2·h−1, respectively. The critical flux and fouling resistances indicated that the fouling propensity increases with the increase of membrane pore size. Two pilot membrane modules with mean pore size of 25nm and 60nm were applied in membrane filtration of surface water treatment. The results showed that serious irreversible membrane fouling occurred on the membrane with pore size of 60nm at the permeate flux of 40.5L·m−2·h−1. On the other hand, membrane with pore size of 25nm exhibited much better anti-fouling performance when permeate flux was set to 40.5, 48 and 60L·m−2·h−1.