Abstract:Ultra-high nickel single-crystal cathode materials have become the most promising for lithium-ion batteries. However, the preparation of ultra-high nickel single-crystal precursors by a continuous coprecipitation method has the disadvantages of large particle size, wide distribution, poor morphology. The extent of the inhomogeneous reactions can be more severe in single-crystal cathodes with larger particle size. Herein, the coprecipitation method with a solid concentrator was adopted, and citrate sodium was used as a complexing agent to improve the physical properties of precursors and electrochemical performance of single-crystal cathode materials. By analyzing the morphology and agglomeration mechanism of the precursor nucleuses under different pH values, it was found that hexagonal nanosheets grew along the 101 direction, and the primary particles showed thicker at pH of 11.4. The hexagonal nanosheets grew along the 001 direction, and the primary particles showed finer at pH of 12.2. The morphology and particle size uniformity of the secondary particles formed by agglomeration at these two pH values showed poor. However, hexagonal nanosheets grew synergistically along the 001 and 101 directions at pH of 11.8, so the primary particles with uniform particle size gradually agglomerated, and then the secondary particles with ultra-small particle size and uniform distribution obtained. Compared to materials prepared by the traditional continuous coprecipitation method, the precursor displays a smaller particle size(D50 = 1.8 µm), higher sphericity, uniformity and denser internal structure. In order to evaluate the performance of Ni0.94Co0.04Mn0.02(OH)2 with ultra-small particle size, the sintering conditions of LiNi0.94Co0.04Mn0.02O2 need to be explored. It was found that the LiNi0.94Co0.04Mn0.02O2 cathode material prepared at 790 °C exhibited higher discharge capacity, cycle and rate performance, compared to materials prepared at 760 °C and 820 °C. We further utilized TEM, EPMA, and XPS to test the internal structure and valence state of LiNi0.94Co0.04Mn0.02O2 cathode material. The results show that the LiNi0.94Co0.04Mn0.02O2 calcined at 790 °C has a good single crystal structure. The LiNi0.94Co0.04Mn0.02O2 cathode materials inherited the structure and particle size of Ni0.94Co0.04Mn0.02(OH)2 precursors, and displayed discharge capacity of 194.7 mAh/g and capacity retention rate of 89.8 % after 100 cycles at 1 C. The microstructure and phase transition of the as-prepared cathode material are well-maintained after long-term cycling, without obvious inter-crystalline micro-crack. The results indicate that its electrochemical performance is better than that of cathode materials with precursors prepared by a continuous coprecipitation method. This work provides new insights for the preparation of small-particle-size precursor and single-crystal cathode materials.

Improvement of cyclicability through precursor treatment in Ni-rich cathode materials

Enhancing high-voltage performances of nickel-based cathode material via aluminum and progressive concentration gradient modification

Facile oxidant-assisted treatment to improve the cyclic performance of Li-rich cathode materials

Enhanced Electrochemical Performance of LiNi0.8Co0.1Mn0.1O2 Cathode for Lithium-Ion Batteries by Precursor Preoxidation

Mitigation of Cation Mixing of LiNiO2-based Cathode Materials by Li-doping for High-Performing Lithium-Ion Battery

Enhancing the electrochemical performance of Li-rich cathode material by a flexible precursor treatment method

Pushing High Capacity with Thermodynamically Stable Interface for Single Crystalline Nickel-rich Cathode

Advances of high-performance LiNi1-x-yCoxMyO2 cathode materials and their precursor particles via co-precipitation process

Stabilizing surface chemical and structural Ni-rich cathode via a non-destructive surface reinforcement strategy

Enhanced electrochemical performance of LiNiO 2 cathode material by precursor preoxidation for lithium-ion batteries

Enhanced Electrochemical Performance of the Layered Nickel-Rich Oxide Cathode by KMnO4 Treatment Precursor

Simultaneous enhancement of ordered layered structure and inhibition of micro-cracks via porous structure to improve stability for Ni-rich cathode

Improving the Cycling Performance of the Layered Ni-Rich Oxide Cathode by Introducing Low-Content Li2mno3

Enhanced Electrochemical Performance of LiNiO2 Cathode Material by Precursor Preoxidation for Lithium-Ion Batteries

Surface Coating with Li-Ti-O to Improve the Electrochemical Performance of Ni-rich Cathode Material

Pre-Deoxidation of Layered Ni-Rich Cathodes to Construct a Stable Interface with Electrolyte for Long Cycling Life

Improving the Structure and Cycling Stability of Ni-Rich Layered Cathodes by Dual Modification of Yttrium Doping and Surface Coating

Improving the Cycle Stability of LiNiO2 through Al3+ Doping and LiAlO2 Coating

Improving the Performance of LiNi0.925Co0.065Mn0.01O2 via Ti4+& Nb5+ Co-Modifications

Enhancing the Reversibility of the Chemical Evolution of the Ni-rich LiNi0.8Co0.1Mn0.1O2 Cathode Via a Simple Pre-Oxidation Process.

Application of precursor with ultra-small particle size and uniform particle distribution for ultra-high nickel single-crystal cathode materials by coprecipitation method