Abstract:Mechanical behaviour of twenty-eight longitudinal lap-welded joints made of high strength steels (HSS) under tension load was investigated by experimental and numerical study. Weaknesses due to traditional deformation measurements for fillet welded joints can be perfectly solved by digital image correlation techniques (DIC). Distribution and development of strain field throughout the specimens along the whole loading process were recorded by DIC measurement. The effect of parameters (e.g. weld size, weld length and mismatch ratio) on mechanical properties (e.g. ultimate strength, failure modes, weld ductility and fracture angle) of longitudinal fillet welds and transverse fillet welds, which was introduced in detail in previous work by the authors, were compared. Generally, because of the difference on the combination of shear force and tension force, the fracture angle of longitudinal welded specimens (around <math>50∘</math>) were much more divergent from transverse welded specimens (around <math>20∘</math>) even though both of them failed at welded zone (welded zone only refers to weld metal in this paper), resulting that the mean strength of longitudinal welded specimens were only 0.58 time of transverse welded specimens. Conversely, the mean deformation capacity of longitudinal welded specimens was almost 4.0 times of transverse welded specimens. All longitudinal welded specimens have "platform" or "decline" feature while all transverse welded specimens have "rise" or "platform" feature load-deformation curves. Generally, the specimens with "rise" feature load-deformation curve are more likely to suffer sudden fracture, while specimens with "decline" or "platform" feature have satisfactory ductility performance. Based on the strain distribution and development features provided by DIC measurement, a new strength criterion, in which the ultimate strain obtained in relevant coupon tests was an indicator, was proposed and through the comparison between the numerical results and test results, its validation was verified by FE simulation. Moreover, it was confirmed that the predicted loads of EC3 and AISC Specification were close and slightly conservative for all specimens.

Load analyses of welded high-strength steel structures using image correlation and diffraction techniques

DIC/DSI Based Studies on the Local Mechanical Behaviors of HR3C/T92 Dissimilar Welded Joint During Plastic Deformation

Residual Stress Evolution during Slot Milling for Repair Welding and Wire Arc Additive Manufacturing of High-Strength Steel Components

In Situ Analysis of Stress and Microstructure Evolution during Welding of High-Alloy Steels Using Energy-Dispersive X-Ray Diffraction

Load‐carrying capacity of MAG butt and fillet welded joints on high‐strength structural steels of grade S960QL and S960MC

An experimental methodology to characterize load-based fracture models of third generation advanced high strength steel resistance spot welds

Digital Image Correlation Structural Strain Analysis of S235 Fillet-Welded Joints under Low-Cycle Fatigue Loadings

Combined Calorimetry, Thermo-Mechanical Analysis and Tensile Test on Welded EN AW-6082 Joints

Welding under service conditions — Resulting weld quality and fatigue strength assessment

IMPLEMENTATION OF LONGITUDINAL WELDING STRESSES INTO STRUCTURAL CALCULATION OF STEEL STRUCTURES

Experimental study on the strength and fracture behaviour of fillet welded joints made of high strength steel under multiple loading angles

Mechanical behaviour of longitudinal lap-welded joints of high strength steel: Experimental and numerical analysis

Welding-induced stresses and distortion in high-strength steel T-joints: Numerical and experimental study

Strain partitioning characterization of advanced high strength steels using in-situ tensile tests with Micro digital image correlation – Methodology and analysis

Synchrotron diffraction residual stresses studies of electron beam welded high strength structural steels

Welding residual stress behavior under mechanical loading

Process-related influences and correlations in wire arc additive manufacturing of high-strength steels

Finite element simulation of multi-layer repair welding and experimental investigation of the residual stress fields in steel welded components

Welded connections at high‐strength steel hollow section joints

Residual stresses of MAG-welded ultrahigh-strength steel rectangular hollow sections

Low-cycle fatigue in ultra-high-strength steel welded joints in the as-welded and post-weld-treated conditions