Preparation of a microsphere SiO2/TiO2 composite pigment: The mechanism of improving pigment properties by SiO2
Sijia Sun,Hao Ding,Jie Wang,Wei Li,Qiang Hao
DOI: https://doi.org/10.1016/j.ceramint.2020.06.068
IF: 5.532
2020-10-01
Ceramics International
Abstract:In this study, a microsphere SiO2/TiO2 composite pigment (M-SiO2/TiO2) was prepared through a facile grinding and calcination process. The structure and properties of M-SiO2/TiO2 were characterized in detail, and the mechanism governing the improvement of pigment properties by M-SiO2 was proposed. The results of this study show that M-SiO2 and TiO2 are successfully compounded, and their combination is inferred to be achieved by the formation of Si-O-Ti bonds through the hydroxyl groups on their surface. The M-SiO2/TiO2 has almost the same pigment properties as pure titanium dioxide, while the weight fraction of TiO2 in M-SiO2/TiO2 is 70%, which can significantly reduce the consumption of TiO2. In M-SiO2/TiO2, the introduction of M-SiO2 leads to the improvement of the rutile-phase conversion of TiO2, as well as reducing TiO2 particle size; thus, this step can further improve the pigment properties. When the calcination temperature is 900 °C, the TiO2 in M-SiO2/TiO2 is primarily rutile (rutile conversion rate is 88.57%) with a particle size of 0.1-0.3 μm, exhibiting good dispersion. In contrast, pure TiO2 is primarily composed of anatase (rutile conversion rate is 11.39%) with a particle size of 0.2-0.6 μm, exhibiting serious agglomeration. The M-SiO2/TiO2 composite is expected to be applied in the fields of paint, plastic, and papermaking in an effort to significantly reduce the cost and consumption of TiO2 pigment.
materials science, ceramics