Abstract:We have demonstrated an anisotropic bulk SmFe12-based sintered magnet with sufficiently large coercivity of μ0Hc=1.0 T and a remanence ratio (Mr/Ms) of 0.84 using conventional liquid sintering process of nitrogen jet-milled powders with the nominal composition of Sm8Fe73.5Ti8V8Ga0.5Al2 (at.%). The moderate saturation magnetization of μ0Ms =0.74 T is due to the dissolution of a large amount of stabilizing elements, Ti, V, and Al, in the 1:12 phase. The anisotropy field of the main 1:12 phase was determined to be µ0HA=10.2 T. Detailed multi-scale microstructure characterizations by scanning electron microscope (SEM) and scanning transmission electron microscope (STEM) showed the magnet consists of Sm(Fe,Ti,V,Al)12 grains with the ThMn12-type crystal structure with a size distribution of ∼3−15µm that are enveloped by ∼3 nm thick Sm-rich amorphous intergranular phase. Secondary phases including metallic (Sm,Ga)-rich, SmOx, and Fe2(Ti,V) phases coexist with the 1:12 phase. Measured angular dependence of coercivity follows Kondorsky type magnetization reversal, suggesting the coercivity arises due to the pining of magnetic domain walls. Magneto-optical Kerr effect (MOKE) microscopy revealed magnetization reversal starts at the grain boundaries and interphase interfaces and thin amorphous intergranular phases act as the pinning sites against magnetic domain wall propagation. Small micromagnetic parameter α∼0.164 estimated by fitting to the Kronmüllar equation suggest that the reduction of the grain size and engineering of the intergranular phase to an Fe-lean composition are necessary to improve the coercivity toward µ0HA/3=3.4 T. This work provides guidelines on an optimum microstructure to develop an anisotropic bulk SmFe12-based sintered magnet with a sufficiently large coercivity.

Temperature stability of coercivity in mischmetal-Fe-Co-B melt-spun ribbons

Magnetic Properties, Thermal Stabilities and Microstructures of Melt-Spun Misch-Metal-Fe-B Alloys

Microstructure Characteristics and Effect of Grain Orientation on Magnetic Properties of Fe 63 Co 32 Gd 5 Alloy Ribbons

Magnetization Process of Nanocrystalline Mischmetal-Fe-b Ribbons

Improvement of coercivity thermal stability of sintered 2:17 SmCo permanent magnet by Nd doping

Microstructure and Magnetic Properties of Melt-Spun Magnetically Anisotropic Sm1+δCo5 Ribbons

The dependence of coercivity on anisotropy field in sintered R-Fe-B permanent magnets

Temperature dependence of magnetization reversal mechanism in misch-metal substituted Nd-Fe-B magnets sintered by dual alloy method

Robustness of magnetocrystalline anisotropy and coercivity in Fe–Co–B

Origin of coercivity in an anisotropic Sm(Fe,Ti,V)12-based sintered magnet

Relation between solidification microstructure and coercivity in MnAl permanent-magnet alloys

Hard magnetic properties and microstructures of melt-spun SmCo5Fex (x = 0, 1 and 2) ribbons

Magnetic properties of melt-spun MM–Fe–B ribbons with different wheel speeds and mischmetal contents

Effect of Fe on Microstructure and Coercivity of Smco-Based Magnets

Microstructure, coercivity and thermal stability of nanostructured (Nd,Ce)-(Fe,Co)-B hot-compacted permanent magnets

Temperature dependences of structure and coercivity for melt-spun MnBi compound

Magnetic Properties and Microstructure of Sm<sub>2</sub>Co<sub>17</sub>-Based High Temperature Permanent Magnet

Microstructure and extrinsic magnetic properties of anisotropic Sm(Fe,Ti,V)12-based sintered magnets

Microstructure and magnetic properties of melt-spun Sm(Co0.58Fe0.31Cu0.04Zr0.05B0.02)z ribbons

Hard magnetic properties and microstructures of melt-spun SmCo<sub>5</sub>Fe<sub><i>x</i></sub>(<i>x</i>= 0, 1 and 2) ribbons

Quantitative analysis of pinning-hardened intrinsic coercivity of Sm(CoFeCuZr)z (z = 7.0–7.8) high-temperature permanent magnets