Abstract:The thermal degradation behaviors of phenylethynyl-terminated polyimide and their carbon fiber reinforced composites (CFRC) are significant to be evaluated comprehensively as their high-temperature applications are gradually expanded. It is found that ether-containing thermoset polyimide (PI) film shows unique degradation behaviors near glass transition temperature ( T g ). Though the triethylamine (Et 3 N) chemical imidization method is applied, the PI backbone shows thermal stability at 371°C thermo-oxidation condition and the main degradation parts site at the curing structure. More aliphatic (C-C) linkages will be formed in the thermo-oxidation process and they are ascribed to the further crosslinking behaviors of polyene structure. However, the PI film shows stable mechanical properties after thermo-oxidation. Meanwhile, the formation of an amorphous carbon structure is found after thermo-oxidation treatment, which endows the composite with enhanced electrical properties. Though the micro-cracking phenomenon happens at the matrix/CF interface of composite surface and thus degrades its mechanical properties, the in-plane longitudinal and transverse conductivity of the composite perform an increase, factors of 1.13 to 2.56×10 4 S/m and 2.28 to 454.8 S/m, respectively. Mechanism study indicates that the formation of amorphous carbon components is caused by the structural rearrangement of the degrading polyene curing structure and becomes more in the thermo-oxidation process, not affecting the backbone integrity and mechanical stability of the PI matrix. As a result, thermo-oxidation treatment degrades the mechanical properties of the composite, whereas the formed amorphous carbon component acts as a self-growing carbon-based nano-filling structure at the PI/CF interface and enhances the electrical contact of the carbon fibers.

Structural evolution from poly(amic acid) to polyimide fibers during thermal imidization process

Effects of pre-imidization on rheological behaviors of polyamic acid solution and thermal mechanical properties of polyimide film: an experiment and molecular dynamics simulation

Preparation and Dielectric Properties of Polyimide/silica Nanocomposite Films Prepared from Sol–gel and Blending Process

Preparation of High-Temperature Resistant Polyimide Fibers by Introducing the p -Phenylenediamine into Kapton-Type Polyimide

Preparation and Property of Polyimide Foams

Synthesis of poly(propylene glycol)-grafted polyimide precursors and preparation of nanoporous polyimides

Synthesis and Properties of a High‐molecular‐weight Poly(amic Acid) and Polyimide Based on 2,2‐Bis(3‐amino‐4‐hydroxyphenyl)hexafluoropropane

Analysis of the kinetics of soluble polyimide formation by the thermal imidization of polyamic acids in amide solvents with allowance for the side reaction of anhydride group hydrolysis

Thermal Degradation Mechanism and Thermal Mechanical Properties of Two High-Performance Aromatic Polyimide Fibers

Study on the Rheological Properties of Fluorinated Polyimide Spinning Solution

Two step synthesis of hydroxyl group polyimide based on 2,2-bis(3-amino-4-hydroxyphenyl)hexafluoropropane

Effect of Initial Molecular Weight on the Structural Evolution of Polyamide 1012 during High-Temperature Thermal Treatments as Revealed by Successive Self-Nucleation and Annealing

Thermal imidization of poly(amic acid) precursors on surface-modified poly(tetrafluoroethylene) films via graft copolymerization with glycidyl methacrylate

Two Step Synthesis of Hydroxyl Group Polyimide Based on 2,2-Bis(amino-4-hydroxyphenyl)hexafluoropropane

Synthesis and Characterization of Thermoplastic Polyether-imide Elastormer

Effect of high-temperature thermo-oxidation on the mechanical and electrical properties of phenylethynyl-terminated polyimide/carbon fiber composite

Synthesis of organosoluble copolyimide and preparation of fibers by dry-spinning process on a large scale

Enhancement of Para-Aramid Fibers by Depositing Poly-P-paraphenylene Terephthalamide Oligomer Modified Multi-Walled Carbon Nanotubes

Effect of the molar mass of polyimide based on pyromellitic dianhydride and 4,4′‐oxydianiline on dielectric and mechanical properties of nonwoven oriented polyimide materials

High Modulus Aliphatic Polyimide from 1, 3-Diaminopropane and Ethylenediaminetetraacetic Dianhydride: Water Soluble to Self-Patterning

Polyether–polyimide Thermoplastic Elastomers. I. Synthesis and Properties