Abstract:Polyamic acid (PAA) fiber derived from 3,3',4,4'-biphenyltetra-carboxylic dianhydride and pphenylenediamine is prepared via dry-jet wet-spinning method. Polyimide (PI) fibers are obtained by applying two kinds of thermal treatment procedures on the PAA fibers. The evolution of fiber structure during thermal treatments is traced. And the influence of fiber structure on the mechanical properties is also studied. In Procedure I, the PAA fibers are heated from room temperature to 400 degrees C at 5 degrees C/min. As temperature increases from room temperature to 125 degrees C, relaxation behavior of PAA chains happens at first. Then, from 125 to 300 degrees C, imidization reaction occurs. Meanwhile, before the temperature reaches 250 degrees C, a significant degradation of PAA chains exists and makes the fibers too weak to measure. Crystals in fiber begin to form as temperature exceeds 250 degrees C and totally complete at 350 degrees C. The fracture strength and initial modulus of fiber are significantly improved with the formation of crystals and finally reach 0.83 GPa and 48.4 GPa at 400 degrees C, respectively. In Procedure II, the PAA fibers are isothermally treated at 250, 300, 350 and 400 degrees C for different times. When treated at 400 and 350 degrees C, both imidization and crystallization in fiber can happen simultaneously and complete in tens of seconds because of the high mobility of the polymer chains. While as treated at 300 and 250 degrees C, both these two processes are slowed down and the formation of crystals lags behind the imidization process. High crystallinity can be obtained under higher treatment temperature in a very short time. The mechanical properties of fiber highly depend on the treatment temperature rather than the treatment time. The fibers treated at 400 degrees C for 60 s show the highest fracture strength and initial modulus of 1.4 GPa and 70.0 GPa, respectively.

Thermal Degradation Mechanism and Thermal Mechanical Properties of Two High-Performance Aromatic Polyimide Fibers

The Crystal Structures and Thermal Shrinkage Properties of Aromatic Polyimide Fibers

Characterizations and Thermal Stability of Soluble Polyimide Derived from Novel Unsymmetrical Diamine Monomers

Synthesis and thermal behaviors of 1,3-bis(4-aminophenoxy)benzene (TPER) and polyimide based on TPER and pyromellitic dianhydride

Thermal Degradation of Organo-Soluble Polyimides

Characterization and Thermal Degradation of Polyimide Derived from 5-Amino-2(p-aminophenyl) Benzoxazole Monomer with Pyromellitic Dianhydride

Study on Syntheses and Properties of Some Novel Polyimides Containing Bisthiazole Rings

Influence of Thermal Treatment on the Structure and Mechanical Properties of One Aromatic BPDA-PDA Polyimide Fiber

Thermal stabilities and the thermal degradation kinetics of polyimides

Study of the Properties of Poly-P-Phenylene-Benzimidazole-Terephthalamide Fiber Material

Preparation and properties of melt-processable polyimides based on fluorinated aromatic diamines and aromatic dianhydrides

Synthesis and Characterization of Highly Soluble Aromatic Polyimides

Synthesis and Property of Fluorenylidene-Containing High Temperature Resistant Polyimides

Low Dielectric and Thermal Properties of Polyimides Based on PMDA, BPADA, TPE-Q and TPE-R

Thermal Degradation Kinetics of Polyimide Containing 2,6-Benzobisoxazole Units

Synthesis and Characterization of Soluble Polyimides Derived from the Polycondensation of 2,6-Bis(4-amino-2-trifluoromethylphenoxy-4 '-Benzoyl)pyridine with Some Aromatic Dianhydrides

Thermal Degradation of the Polyimide Synthesized from 4,4′‐(hexafluoroisopropylidene) Diphthalic Dianhydride and 4,4′‐Diaminodiphenylmethane

Preparation and characterization of aromatic polyimides derived from 4,4′-oxydiphthalic anhydride and 4,4′-diaminodiphenylmethane with different alkyl substituents

Thermal properties of the polyimide foam prepared from aromatic dianhydride and isocyanate

Investigation of the Solution Behavior of Organosoluble Aromatic Polyimides

Synthesis and characterization of novel polyimides derived from 2,6-bis[4-(3,4-dicarboxyphenoxy)benzoyl]pyridine dianhydride and aromatic diamines