Abstract:Ultrasonic impact treatment of stainless steel AISI 321 was carried out at room temperature (in the argon environment – argon-UIT) and at cryogenic temperature (in liquid nitrogen – cryo-UIT) in the constrained conditions with application of the same mechanical energy to the treated specimens. The time dependencies of the surface hardness HV after the cryo-UIT and argon-UIT processes were of sigmoidal and parabolic shapes, respectively. The microstructural evolution of the surface layers of the deformed specimens was studied by X-ray diffraction (XRD), optical microscopy (OM), transmission electron microscopy (TEM) and selective area electron diffraction (SAED) analyses. The volume fractions of the deformation-induced α′ (V α′) and ε (V ε) martensites were estimated using XRD approach and by magnetic and density measurements. Compared to the room temperature UIT in the argon environment (argon-UIT), the liquid nitrogen UIT generates a higher density of the deformation twins and stacking faults. In addition, a higher V α′ (~53%) and V ε (~3.5%) were observed after cryo-UIT in deeper surface layers (~200μm). The argon-UIT process leads to the formation of either rectangular twin blocks or dislocation cells, which size ranged 200–500nm. Conversely, after cryo-UIT (ē ≈0.95), a nanoscale grain structure of heterogeneous nature (α′ and γ phases) was formed in the outmost surface layer simultaneously with the areas filled with networks of deformation twins and stacking faults. The minimum grain size of α′-martensite D α′ and austenite D γ was respectively 25 and 45nm, and twin thickness/spacing was of 60–120nm. Both types of the microstructure contribute to the material strength and result in higher hardness of the cryo-UIT processed specimens (~5–5.66GPa) compared to that of the argon-UIT processed ones (~4.3GPa). With the increase in Zener-Hollomon parameter lnZ, the grain/twin/spacing size is decreased while the V α′ and surface microhardness HV are increased.

Impact of surface preparation on the formation of deformation-induced α‘-martensite in a metastable austenitic steel

Strain-induced Refinement and Thermal Stability of a Nanocrystalline Steel Produced by Surface Mechanical Attritiontreatment

Electropolishing study of metastable austenitic steel AISI 347 for EBSD analyses

Effect of Surface Roughness and Chemical Composition of Metastable Austenitic Stainless Steels on Electrochemical Polishing-Induced Martensitic Transformation

AFM for diagnosis of nanocrystallization of steels in hardening processes

Martensitic transformation during electrochemical polishing of metastable austenitic stainless steel

Investigations of Metallurgical Differences in AISI 347 and Their Influence on Deformation and Transformation Behaviour and Resulting Fatigue Life

Nitriding behavior and corrosion properties of AISI 304L and 316L austenitic stainless steel with deformation-induced martensite

Effects of ultrasonic nanocrystal surface modification on the surface integrity, microstructure, and wear resistance of 300M martensitic ultra-high strength steel

Successive Grinding and Polishing Effect on the Retained Austenite in the Surface of 42CrMo4 Steel

Martensitic Transformation and Work Hardening of Metastable Austenite Induced by Abrasion in Austenitic Fe-C-Cr-Mn-B Alloy - A Tem Study

Characterization of the Nano-Scale Surface Layer of a Tempered Martensitic Steel Synthesized by Ultrasonic Nanocrystalline Surface Modification Treatment

Mechanical Surface Treatments of AISI 304 Stainless Steel: Effects on Surface Microrelief, Residual Stress, and Microstructure

Effect of Plastic Deformation on Microstructure and Properties of 347 Austenite Steel.

Influence of microstructural features and deformation-induced martensite on hardening of stainless steel by cryogenic ultrasonic impact treatment

Electrochemically induced annealing of stainless-steel surfaces

Bending fatigue behavior of metastable and stable austenitic stainless steels with different surface morphologies

Structural Transformations and Tribological Effects in the Surface Layer of Austenitic Chrome-Nickel Steel Initiated by Nanostructuring and Oxidation

The Use of Strain-Induced Martensitic Transformation Phenomena to Estimate the Surface Plastic Strain Produced by Grit Blasting on Overaged 18Ni Maraging Steel

Microstructure of Laser Hardened Martensitic High Nitrogen Steel Subsurfaces

Microstructure evolution and mechanical properties of martensite stainless steel during repetitive high stress Loading-Unloading with small plastic deformation