Abstract:Ultrasonic impact treatment of stainless steel AISI 321 was carried out at room temperature (in the argon environment – argon-UIT) and at cryogenic temperature (in liquid nitrogen – cryo-UIT) in the constrained conditions with application of the same mechanical energy to the treated specimens. The time dependencies of the surface hardness HV after the cryo-UIT and argon-UIT processes were of sigmoidal and parabolic shapes, respectively. The microstructural evolution of the surface layers of the deformed specimens was studied by X-ray diffraction (XRD), optical microscopy (OM), transmission electron microscopy (TEM) and selective area electron diffraction (SAED) analyses. The volume fractions of the deformation-induced α′ (V α′) and ε (V ε) martensites were estimated using XRD approach and by magnetic and density measurements. Compared to the room temperature UIT in the argon environment (argon-UIT), the liquid nitrogen UIT generates a higher density of the deformation twins and stacking faults. In addition, a higher V α′ (~53%) and V ε (~3.5%) were observed after cryo-UIT in deeper surface layers (~200μm). The argon-UIT process leads to the formation of either rectangular twin blocks or dislocation cells, which size ranged 200–500nm. Conversely, after cryo-UIT (ē ≈0.95), a nanoscale grain structure of heterogeneous nature (α′ and γ phases) was formed in the outmost surface layer simultaneously with the areas filled with networks of deformation twins and stacking faults. The minimum grain size of α′-martensite D α′ and austenite D γ was respectively 25 and 45nm, and twin thickness/spacing was of 60–120nm. Both types of the microstructure contribute to the material strength and result in higher hardness of the cryo-UIT processed specimens (~5–5.66GPa) compared to that of the argon-UIT processed ones (~4.3GPa). With the increase in Zener-Hollomon parameter lnZ, the grain/twin/spacing size is decreased while the V α′ and surface microhardness HV are increased.

Influence of microstructural features and deformation-induced martensite on hardening of stainless steel by cryogenic ultrasonic impact treatment

The Effect of Cryogenic Treatment Temperature on the Mechanical Properties and Microstructure of 440C Martensitic Stainless Steel

Deformation microstructures and martensitic transformation pathways in cryogenically deformed 316L stainless steel

Low-Temperature Impact Property of 0Cr17Mn17Mo3NiN AusteniticStainless Steel after Cryogenic Treatment

Enhancing Ductility of Martensitic Steels Through Cryogenic Treatment

Elucidating the role of secondary cryogenic treatment on mechanical properties of a martensitic ultra-high strength stainless steel

Microstructural variations and mechanical properties of deep cryogenic treated AISI M35 high-speed steel tempered at various temperatures

The Microstructure, Tensile and Impact Properties of Low-Activation Ferritic-Martensitic Steel EK-181 after High-Temperature Thermomechanical Treatment

Effect of ultrasonic surface impact on the microstructural characterization and mechanical properties of 316L austenitic stainless steel

Mechanical Surface Treatments of AISI 304 Stainless Steel: Effects on Surface Microrelief, Residual Stress, and Microstructure

Effect of Deep Cryogenic Time on Martensite Multi-Level Microstructures and Mechanical Properties in AISI M35 High-Speed Steel

The effects of room temperature soaking and deep cryogenic treatment on the stress relief phenomenon of Ti-Mo maraging stainless steel

Cryogenic Treatment of Martensitic Steels: Microstructural Fundamentals and Implications for Mechanical Properties and Wear and Corrosion Performance

Case Study of the Tensile Fracture Investigation of Additive Manufactured Austenitic Stainless Steels Treated at Cryogenic Conditions

Effect of cryogenic treatment on the mechanical properties of 4340 steel

Effect of annealing temperature on microstructure and properties of stainless steel rings after high-pressure torsion

Increasing the Wear Resistance of Parts Made of High-Alloy Steels for Cold-Forming Using Cryogenic Treatment

Study of Cryogenic Treatment on the Microstructure and Mechanical Properties of Marine 10Ni5CrMoV Steel

Strength‐Ductility Synergy in an Austenitic Stainless Steel Processed by Warm Rolling and Subsequent Cryogenic Treatment

Study on Hardness and Elastic Modulus of Surface Nanostructured 304 Stainless Steel Using Two Mechanical Methods

Martensitic transformation in rolled 301 stainless steel induced by cryogenic treatment