Abstract:Herein, the cryogenically martensitic transformation and its effects on the tempering behaviors of bearing steel was investigated. An in-situ magnetic method was used for obtaining the thermodynamics of the martensitic transformation at sub-zero Celsius temperature from in respects of athermal and isothermal conditions. Microstructure evolution was also characterized systematically to investigate the mechanisms of the martensitic transformation. The results showed that the athermally martensitic transformation of samples experienced three different stages, where the martensite formed slowly at 300–230 K, rapidly at 230–120 K, and slowly again at 120–77 K during the continuous cooling process. With the increase of cooling rate, both the start and finish temperatures of the transformation rise, while the maximum transformed rate decreases. The content of retained austenite transformed isothermally is much smaller as compared to the athermal condition. The amount of isothermally formed martensite does not show linear relationship with the temperature, where an optimal isothermal temperature for GCr15 steel is 193 K in this work. XRD measurement result showed that the content of retained austenite decreased with the decrease of treating temperature in practical DCT, where the content was reduced up to 4.2% after DCT at the lowest temperature combined with tempering. DCT enhanced the precipitation of θ-carbides during tempering and altered the precipitation behavior by advancing the precipitated temperature of θ-carbides from 340 °C to 315 °C. The tempered hardness of samples was improved by DCT, which can be attributed to the enhanced carbides precipitation during tempering and lower content of retained austenite after DCT. The improvement was also affected by tempering and austenitizing temperatures. It was concluded that the performance improvement induced by DCT was most evident if DCT was conducted between higher temperature quenching and lower temperature tempering. DCT also affected the decomposition of retained austenite during tempering by decreasing the activation energy of decomposition by up to 38.13 KJ/mol, which indicated a lower thermal stability of retained austenite after DCT. Microstructure observation indicated that the substructure of the new formed martensite was dominated by ultra-fine twins, which derived from the accommodated strain induced by martensitic transformation during DCT. The transformation strain induced by DCT also causes more dislocations in the microstructure, which provides more nucleation sites for the precipitation of θ-carbides during tempering.

Study of Cryogenic Treatment on the Microstructure and Mechanical Properties of Marine 10Ni5CrMoV Steel

Effect of tempering and deep cryogenic treatment on microstructure and mechanical properties of Cr–Mo–V–Ni steel

The Effect of Multi-Step Tempering and Partition Heat Treatment on 25cr2ni3mov Steel’s Cryogenic Strength Properties

Study on Microstructure and Mechanical Properties of Marine 10Ni5CrMoV Steel during Tempering

Enhancing Ductility of Martensitic Steels Through Cryogenic Treatment

Effect of Deep Cryogenic Time on the Microstructure and Mechanical Property of Cr-Mn-Si High-Strength Alloy Steel

Effect of aging temperature on the heterogeneous microstructure and mechanical properties of a 12Cr–10Ni–Mo–Ti maraging steel for cryogenic applications

Tailoring the Microstructure to Enhance the Cryogenic Mechanical Properties of a Fe–34.5mn–0.04c Steel

Effect of aging temperature on the austenite reversion and mechanical properties of a Fe–10Cr–10Ni cryogenic maraging steel

Effects of traditional heat treatment and a novel deep cryogenic treatment on microstructure and mechanical properties of low-carbon high-alloy martensitic bearing steel

Enhanced Mechanical Properties and Ultrafine Microstructure of 18CrNiMo7-6 Steel Prepared by Quenching and Partitioning Combined Cryogenic Treatment

The Strengthening Role of Cryogenic Treatment in the Mechanical Properties and Abrasive Wear of Low Alloy Wear-Resistant Steel

Microstructure and mechanical properties in core of a carburizing 20CrNi2MoV bearing steel subjected to cryogenic treatment

Impact toughness and fracture behaviour of a lamellar structural Fe–Mn–Al–C cryogenic steel

Effects of Cryogenic Treatment and Tempering on Mechanical Properties and Microstructure of 0.25C-0.80Si-1.6Mn Steel

Cryogenically martensitic transformation and its effects on tempering behaviors of bearing steel

Effect of Modifying Matrix Microstructures and Nanosized Precipitates on Strengthening Mechanisms and Ductile-to-brittle-transition-temperature in a 1000 MPa Ni–Cr–Mo–Cu Steel

Effect of Deep Cryogenic Time on Martensite Multi-Level Microstructures and Mechanical Properties in AISI M35 High-Speed Steel

Thermomechanical Analysis of Deep Cryogenic Treatment of Navy C-Ring Specimen

Influence of Intercritical Temperature on the Microstructure and Mechanical Properties of 6.5 Pct Ni Steel Processed by Ultra-fast Cooling, Intercritical Quenching and Tempering

Effect of multiple deep cryo-treating and tempering on microstructure and property evolution of high carbon bearing steel