Increasing the Wear Resistance of Parts Made of High-Alloy Steels for Cold-Forming Using Cryogenic Treatment

S. A. Zemlyakov,M. A. Guryev,A. M. Guryev,Guryev, A. M.

DOI: https://doi.org/10.1134/s1063785023700062

2023-12-21

Technical Physics Letters

Abstract:The paper presents the results of metallographic analysis of the microstructure of high-alloy Uddeholm Sverker 3 steel (AISI Type D2). Cold treatment of high-alloy steels is used as a way to reduce the amount of retained austenite and, as a consequence, to stabilize the mechanical properties and dimensions of precision parts. In this work, we have used deep cold treatment by immersion in liquid nitrogen after heat treatment according to the traditional technology (quenching for primary hardness and low tempering). Exposure to liquid nitrogen has been carried out for 24 h. At the end of the exposure, the parts have been removed from liquid nitrogen and kept at room temperature until they reached room temperature. Then, the parts have been subjected to tempering at a low temperature of 170°C. The cryogenically treated sample has more noticeable fluctuations in the chemical composition and a larger amount of the carbide phase (30 and 27 vol %, respectively). Fluctuations in the chemical composition are expressed in more intense coloring of carbide particles using color etching, which indicates differences in their chemical composition. In the case of cryogenic treatment, the average specific size of carbides is less than in the absence of it. In addition, an increase in the content of ultrafine carbides is observed in the cold-treated sample, which is logically explained by their precipitation from retained austenite during its decomposition at cryogenic temperatures, decay of retained austenite and, as a result, the release of additional volumes of carbide particles. Particles formed during cryogenic treatment can be classified as ultrafine, with an average diameter of about 1 μm.

physics, applied