Abstract:Additive manufacturing (AM) technology for metallic alloys such as laser powder bed fusion (LPBF) brings tremendous opportunities for development of novel alloys specifically designed for AM that would desensitize the inherent process variability and requires a refined understanding of processing–structure–property relationship that would contribute to future alloy development. In this study, two different alloys, Al-6Zn-2Mg and Al-6Zn-2Mg-0.7Sc-0.3Zr in wt. pct, representing traditional and AM-specific novel aluminum alloys, respectively, were manufactured by LPBF technique using pre-alloyed gas atomized powders. The Al-Zn-Mg ternary alloys exhibited cracks at various LPBF processing parameters, primarily along the grain boundaries of the large columnar grains that extended across multiple melt pools. The severity of cracking in LPBF Al-Zn-Mg alloys was process-dependent and could be correlated to the change in alloy composition due to evaporation of Zn and Mg with high vapor pressure. The Scheil–Gulliver non-equilibrium solidification calculations showed that the Al-Zn-Mg alloys with lower Zn and Mg concentrations had smaller solidification range (i.e., ΔT) and steepness values (i.e., dT/dfs1/2$$ \left| {{\text{d}}T / {\text{d}}f_{\text{s}}^{1/2} } \right| $$ near fs1/2=1$$ f_{\text{s}}^{1/2} = 1 $$), which corresponded to a lower cracking severity. On the other hand, no cracks were observed in Al-Zn-Mg-Sc-Zr alloys, although their solidification range and steepness values were similar to the ternary Al-Zn-Mg alloys. The microstructure of Al-Zn-Mg-Sc-Zr alloys exhibited a much refined heterogeneous microstructure containing small equiaxed and columnar grains within each melt pool, owing to the heterogeneous nucleation upon primary Al3(Sc,Zr) particles. Process-dependent microstructure was observed as a result of variation in thermal gradient and cooling rate associated with LPBF parameters. Findings from this study provide guidance for the future design of AM-specific aluminum alloys and insights into the microstructural control by LPBF.

Mechanical Anisotropy Investigated in the Complex SLM‐Processed Sc‐ and Zr‐Modified Al–Mg Alloy Microstructure

Novel isotropic mechanical properties of laser powder-bed fusion Sc/Zr modified Al alloy

Microstructure-induced anisotropic tribological properties of Sc-Zr modified Al–Mg alloy (Scalmalloy®) produced via laser powder bed fusion process

In-situ Investigation of the Anisotropic Mechanical Properties of Laser Direct Metal Deposition Ti6Al4V Alloy

Microstructure and Mechanical Properties of Selective Laser Melted Mg-9 Wt%al Powder Mixture

Thermal and mechanical properties of an Al-Mg-Sc-Zr high strength alloy fabricated by selective laser melting

Role of nitrogen and helium gases on microstructure and anisotropic mechanical properties of cold-sprayed scalmalloy deposits

Comparison of Microstructure and Mechanical Properties of Scalmalloy® Produced by Selective Laser Melting and Laser Metal Deposition

Rotating Scan Strategy Induced Anisotropic Microstructural and Mechanical Behavior of Selective Laser Melted Materials and Their Reduction by Heat Treatments

Deformation effect of melt pool boundaries on the mechanical property anisotropy in the SLM AlSi10Mg

Microstructure and Mechanical Properties of an Er-Modified Al–Mg–Mn–Sc–Zr Alloy Processed by Selective Laser Melting

Microstructural evolution modelling and low-stress fatigue performance of bimodal-structured Al-Mg-Sc-Zr alloy produced by laser powder bed fusion additive manufacturing

Tensile property and microstructure of Al−4.77Mn−1.37Mg−0.67Sc−0.25Zr alloy under different selective laser melting processing parameters

In-situ mechanical and microstructural characterization of miniaturized Al-Mg-Sc-Zr and AlSi10Mg specimens processed by laser powder-bed fusion (PBF-LB)

Influence of Manufacturing Geometric Defects on the Mechanical Properties of AlSi10Mg Alloy Fabricated by Selective Laser Melting

Process-Dependent Composition, Microstructure, and Printability of Al-Zn-Mg and Al-Zn-Mg-Sc-Zr Alloys Manufactured by Laser Powder Bed Fusion

Selective Laser Melting of Gas Atomized Al–3.02Mg–0.2Sc–0.1Zr Alloy Powder: Microstructure and Mechanical Properties

Superior mechanical properties of a selective-laser-melted AlZnMgCuScZr alloy enabled by a tunable hierarchical microstructure and dual-nanoprecipitation

Microstructural Evaluation and Tensile Properties of Al-Mg-Sc-Zr Alloys Prepared by LPBF

Effect of Heat Treatment on the Anisotropy in Mechanical Properties of Selective Laser Melted AlSi10Mg

Developing a high-strength Al-Mg-Si-Sc-Zr alloy for selective laser melting: Crack-inhibiting and multiple strengthening mechanisms