Ethylene Vinyl Alcohol Copolymer (EVOH) as a Functional Barrier against Surrogate Components Migrating from Paperboard

Caroline Maes,Giberto Mitsuyoshi Yuki Junior,Cynthia Teniers,Wout Luyten,Geert Herremans,Roos Peeters,Pieter Samyn,Robert Carleer,Mieke Buntinx
DOI: https://doi.org/10.1155/2019/4180708
2019-01-01
Journal of Chemistry
Abstract:Ethylene vinyl alcohol copolymer (EVOH) is a key material of interest as a functional barrier against substances migrating from recycled paperboard, due to its outstanding barrier properties. Three multilayer films containing two different grades of EVOH, L171B (3 μ m) and F171B (3 and 5 μ m), were benchmarked against a multilayer film containing polyamide 6/6.6 copolymer (PA 6/6.6, 3 μ m) and monolayer polyethylene terephthalate (PET, 12 μ m). The 5 films were evaluated as barrier materials against 5 surrogate substances simulating different migrants potentially present in recycled paperboard: n -heptadecane (C17) as a mineral oil-saturated hydrocarbon (MOSH), 4-methylbenzophenone (MBP) as a photoinitiator, di- n- propyl phthalate (DPP) as a plasticiser, and anthracene (ANT) and perylene (PER) as mineral oil aromatic hydrocarbons (MOAHs). The test was accelerated at 60°C for 25 days, which is equivalent to a shelf life of 2 years at 25°C. All films containing 3 or 5 μ m EVOH were found to be good barriers, showing no breakthrough values over 1% of the initial concentration found in the paperboard, and they could easily compete with 12 μ m PET. The multilayer with 3 μ m PA 6/6.6 showed higher breakthrough values for both MBP and DPP than the other materials although still below the 1% threshold value. However, ANT showed substantial breakthrough values of nearly 2%, indicating that PA 6/6.6 might not offer enough protection against low-weight MOAH components.
chemistry, multidisciplinary
What problem does this paper attempt to address?