Abstract:Studying the dynamic failure laws of metal materials and structures under blast and impact loading through numerical simulation is of great significance for characterizing the damage effects of explosive shock and designing novel impact-resistant structures. The metals’ failure under strong dynamic loading involves multiple complex physical processes, such as the large deformation, the thermo-mechanical coupling and the material state changes. These complex physical processes bring great challenges to numerical simulation, including the geometric description of complex dynamic failure modes such as cracks and shear bands, the determination of failure criteria and the description of plasticity-damage coupled evolution, etc. In response to these challenging issues, a theoretical and computational thermal elasto-plastic phase field model was established based on the energy variational principle to describe metals' dynamic failure. For the model, a unified description of the crack and shear band was realized, and an efficient solving strategy of explicit finite elements was proposed. The model was further applied to 3 typical metals’ dynamic failure issues under blast and impact loading: the transition between brittle and ductile failure modes of metals, the self-organization of adiabatic shear bands (ASBs) and the transition between failure modes of thin-walled disks under shock waves. The results verify the accuracy of the theoretical model and the robustness of the computational model. This work lays a foundation for the subsequent development of damage assessment and protective structure design against blast and impact loading based on simulation.

High Plastic Deformations and High Cooling Rates at the Interface of Explosion-Welded Materials

Numerical Simulation of a High-Speed Impact of Metal Plates Using a Three-Fluid Model

INFLUENCE HOT PLASTIC DEFORMATION ON THE STRUCTURE AND PROPERTIES OF CARBON STEEL OF THE RAILWAY WHEEL

Interfacial investigations on the microstructure evolution and thermomechanical behavior of explosive welded CLAM/316L composite

Advances in Numerical Simulation of High-Speed Impact Welding

Mechanisms of Intragrain Plastic Deformation in Steel Heating Process

Stability of permanent connection of deformable high-temperature nickel based and cast intermetallic alloys obtained under superplasticity conditions

Plastic Deformation of Metal Tubes Subjected to Lateral Blast Loads

Experimental and Numerical Investigations of Composite Plates Under Impact Load

Stability of permanent connection of deformable high-temperature nickel based and cast intermetallic alloys obtained by pressure welding under superplasticity conditions

A Study on Explosion Welding Defects of Large-Sized Plates

New Solution for Plastic Deformation Process Intensification

Interfacial surface relief in explosive welding of homogeneous materials

Numerical and experimental studies of the interface characteristics and wave formation mechanism of Hastelloy/stainless steel explosive welding composite plate

Study on defects of large-sized Ti/steel composite materials in explosive welding

Novel severe plastic deformation method for extrusion compression composite processing

Microstructure Evolution and Growth of Interfacial Intermetallic Compounds in NiCr/Ti Alloy Laminated Composite after Explosive Welding and Heat Treatment

Mathematical modelling of the effect of the surface relief of specimens on the localisation of plastic deformation in the pressure welding zone

Dynamic Failure Simulation of Metal Materials and Structures under Blast and Impact Loading

A rate-dependent damage mechanics model for predicting plasticity and ductile fracture behavior of sheet metals at high strain rates

FORMATION OF THE STRUCTURE AND COMPOSITION OF THE DIFFUSION INTERACTION ZONE DURING THE HEAT TREATMENT OF THE EXPLOSION-WELDED AD1 + Cr20Ni80 COMPOSITE IN THE PRESENCE OF A LIQUID PHASE