Optimization of Hot Backward Extrusion Process Parameters for Thin-Walled Tubes of Mg-9Gd-3Y Alloy Based on 3D Processing Maps
Jian Zeng,Shuai Dong,Fenghua Wang,Fulin Wang,Li Jin,Jie Dong
DOI: https://doi.org/10.1007/s11665-024-10250-x
IF: 2.3
2024-10-11
Journal of Materials Engineering and Performance
Abstract:In this research, the cast-homogenized Mg-9Gd-3Y (GW93) alloy was subjected to isothermal hot compression tests at different temperatures ranging from 300 to 450 °C and different strain rates from 0.001 to 1 s -1 , and its hot compression deformation characteristic was studied. With the aid of the dynamic material model and the Murty instability criterion, a 3-dimensional (3D) hot processing map describing the intrinsic processability of the material was established. Through the secondary development, the 3D hot processing map of GW93 alloy was then imported into the finite element software DEFORM-3D, implementing backward extrusion forming simulation of thin-walled tubes under various process parameters. The power dissipation coefficient was utilized to evaluate the material's formability after the deformation. The effects of deformation temperature and extrusion speed on the formability of thin-walled tubes were studied, and the process parameters were optimized to 430 °C and 0.25 mm/s. Afterward, the thin-walled tubes with an outer diameter of 40 mm, wall thickness of 2 mm and height of 50 mm were prepared by practical backward extrusion experiments under 3 different groups of parameters. The present study suggests that under the parameters of 430 °C and 0.25 mm/s, the thin-walled tube was granted with an intact appearance and undergo a secure deformation. Furthermore, its microstructure was characterized by the presence of fine recrystallized grains. The surfaces of the thin-walled tubes would be prone to cracking under the other 2 groups of parameters (430 °C/0.1 mm/s and 410 °C/0.25 mm/s), with clearly visible cracks observed under an optical microscope.
materials science, multidisciplinary