Abstract:Here, a new Mg-1Bi-1Mn-0.3Zn (BMZ110, wt%) wrought alloy designed by the dilute addition of Zn subjected to an appropriate extrusion processing that showed an excellent strength-ductility synergy at room temperature. The main results included four aspects as follows: 1) With dilute Zn addition, the as-cast BMZ110 alloy was refined into an approximately equiaxed-grained structure, since the solid solution of Zn provided a relatively high growth restriction factor. 2) The as-extruded BMZ110 alloy exhibited the finer average grain size and weaker basal texture intensity than the as-extruded BM11 alloy without Zn. The co-segregation of Bi and Zn solutes into grain boundaries was observed to impede grain growth during extrusion and further weaken texture intensity. Moreover, Zn atoms incorporated into Mg3Bi2 phases by replacing Bi atoms increasing the nucleation rate of Mg3Bi2 phases and refining their sizes. 3) Compared with the as-extruded BM11 alloy, the as-extruded BMZ110 alloy demonstrated the higher yield strength (~ 283.4 MPa), ultimate strength (~ 366.2 MPa) and elongation-to-failure (~ 26%). The size refinement of grains and second phases contributed to an extra strength increments. Grain boundary segregation enhanced grain boundary cohesion not only reducing the number density of grain boundary cracks, but also activating more slip modes and grain rotation for increasing the ductility. 4) The as-extruded BMZ110 alloy had the higher grain growth resistance than the as-extruded BM11 alloy during annealing. Solute segregation offered an effective obstacle to restrict grain boundary migration enlarging the activation energy (~ 112.2 kJ/mol) and further delaying the grain growth. Therefore, this work will be helpful for the development of new high performance low-alloyed Mg-Bi based wrought alloys to achieve extensive applications in industries.

High ductility induced by un-DRXed grains in a Mg–Zn–Mn–La–Ce alloy

Low-cost and high-strength Mg-Al-Ca-Zn-Mn wrought alloy with balanced ductility

Mechanistic investigation of a low-alloy Mg–Ca-based extrusion alloy with high strength–ductility synergy

A rolled Mg−8Al−0.5Zn−0.8Ce alloy with high strength-ductility synergy via engineering high-density low angle boundaries

Enhanced strength-ductility synergy and activation of non-basal slip in as-extruded Mg–Zn–Ca alloy via heterostructure

Tailoring strength and ductility of Mg97Y2Zn1 alloy through the architecture of heterogeneous lamellar structure by large-ratio hot extrusion

Achieving High Strength-Ductility Synergy in Low-Alloyed Mg-Li-Er Extrusion Alloys via Tailoring Bimodal-Grained Structure

Achieving excellent strength-ductility combination of Al-aided Mg-Gd-Al-Zr-Zn alloys fabricated by cold metal transfer-based wire-arc directed energy deposition via uniform equiaxed grains and multiple precipitates

Preparation of ultrafine-grained Mg–Mn–Ce alloy with high ductility and energy absorption by coupling extrusion and forging

Development of low rare-earth containing magnesium alloy with high strength-ductility synergy by engineering nano-spaced lamellae

Exploiting an as-extruded fine-grained Mg-Bi-Mn alloy with strength-ductility synergy via dilute Zn addition

Revealing the influence of Zr micro-alloying and hot extrusion on a novel high ductility Zn–1Mg alloy

Fabrication of high strength-ductility Mg-3.8Al-1.1Sn-0.4Ca alloy via differential-thermal asymmetric extrusion

High strength and high ductility achieved in a heterogeneous lamella-structured magnesium alloy

High Performance Mg Alloy with Designed Microstructure and Phases

Development and characteristics of a low rare-earth containing magnesium alloy with high strength-ductility synergy

Achieving exceptional ultrahigh-strength in low-alloy Mg-1Al-1Ca-0.4Mn (wt%) alloy by regulating bimodal microstructure

Development of low-alloyed Mg–Zn–Ca–Sn–Mn alloy with high strength-ductility synergy by sub-rapid solidification and hot rolling

Realizing ultra-fine grains and ultra-high strength in conventionally extruded Mg-Ca-Al-Zn-Mn alloys: The multiple roles of nano-precipitations

Superior Strength-Ductility Synergy of Mg-Nd-Zn-Zr Alloy Rod Achieved by Drawing at Elevated Temperatures

Fine-grained Mg–1Mn–0.5Al–0.5Ca–0.5Zn alloy with high strength and good ductility fabricated by conventional extrusion