Abstract:The rapid growth of the Li-ion battery (LIB) market has greatly driven research on LIBs, particularly on LIB failure mechanisms under different operating conditions (long-term cycling, overcharge, over-discharge, high temperatures, low temperatures, etc.) due to safety issues1. Up to now, there are only very few of reports on the capacity fade mechanisms in the commercial batteries2. It is paramount of scientific and engineering importance to understand the microstructure evolution during normal cycle in the commercial cells. To our knowledge, in situ monitoring of microstructure evolution during the capacity fade process in either a commercial battery or lab-made batteries has never been reported before. In this work, the capacity fade/failure processes of commercial 18650 LiFePO4 cell during the long term normal charge/discharge, overcharge, and over-discharge cycling was systematically investigated respectively. The commercial 18650 LiFePO4cells (A123 Systems) were chosen to be cycled for all cycling conditions until these cells reach 80% of initial capacity (typical criteria for EV application) or cannot be charged/discharged. The cells were in situ characterized and the microstructure of the electrodes was investigated using synchrotron high-energy X-ray diffraction during long term normal cycling and overcharge/over-discharge cycling conditions. Synchrotron high-energy X-rays with photon energy of 115 KeV are capable of penetrate through thick samples, which allows us to probe commercial 18650 LiFePO4 cells without any cell modification and the results are presented herein. The result of 18650 cell after 2500 cycles is shown in Fig. 1. Our in situ experiment result show that loss of the active lithium source in the system is the primary cause of the capacity fade and the appearance of the inactive FePO4phase is proportional to the decrease of available lithium source during cycling. Electrochemical Impedance Spectroscopy (EIS) is a powerful and quick analytical and diagnostic tool that can be used to study the internal resistance of Li-ion batteries during long-term normal cycling or overcharge/ over-discharge cycling3. The EIS results during overcharge and over-discharge process are shown in Fig. 2 and 3 respectively, and the de-convoluted Ohmic resistance, solid electrolyte interphase (SEI) resistance, and Warburg Coefficient, change with cycle number in some patterns, indicating the occurrence of corrosion of the current collector, SEI breakdown/decomposition and reformation, and the development of diffusion barriers of Li+ in the electrode, respectively. These parameters are associated with failure and can be used as indicators of incoming failure. Overall, EIS can be used as an effective and reliable tool to monitor the state of health, predict incoming failure of the LIB cells, and issue a warning before failure without disturbing the operation of the cells. Figure 1

Experimental analysis on lithium iron phosphate battery over-discharged to failure

Impact of Low Temperature Exposure on Lithium-Ion Batteries: A Multi-Scale Study of Performance Degradation, Predictive Signals and Underlying Mechanisms

Investigation of a commercial lithium-ion battery under overcharge/over-discharge failure conditions

Experimental investigations on the correlations between the structure and thermal‐electrochemical properties of over‐discharged ternary/ Si‐C power batteries

Experimental research on thermal runaway characterization and mechanism induced by the shell insulation failure for LiFePO 4 Lithium-ion battery

Investigation on the root cause of the decreased performances in the overcharged lithium iron phosphate battery

Impact of low temperature and charge profile on the aging of lithium-ion battery: Non-invasive and post-mortem analysis

Experimental Study on High-Temperature Cycling Aging of Large-Capacity Lithium Iron Phosphate Batteries

Influence of Over-Discharge on the Lifetime and Performance of LiFePO4/graphite Batteries

Aging Mechanisms and Evolution Patterns of Commercial LiFePO4 Lithium-Ion Batteries

Thermal behavior and failure mechanisms of 18650 lithium ion battery induced by overcharging cycling

A Comparative Study of Overdischarge Behaviors of Cathode Materials for Lithium-Ion Batteries

Sensitivities of lithium-ion batteries with different capacities to overcharge/over-discharge

Failure mechanism and voltage regulation strategy of low N/P ratio lithium iron phosphate battery

Analysis of the Discharge Termination Mechanism of a Nonaqueous Li-O2 Battery Based on a Digital Reconstruction Model

Failure Mechanism Investigation of Commercial LiFePO4 Cells in Different Operating Conditions

Overcharge-Induced Capacity Fading Analysis for Large Format Lithium-Ion Batteries with Liyni1/3co1/3mn1/3o2 + Liymn2o4 Composite Cathode

Unrevealing the effects of low temperature on cycling life of 21700-type cylindrical Li-ion batteries

Failure Investigation of LiFePO4 Cells under Overcharge Conditions

Study on Thermal Safety of the Overcharged Lithium-Ion Battery

Experimental study on charicteristics of overdischarged Li-NCM batteries