Unrevealing the effects of low temperature on cycling life of 21700-type cylindrical Li-ion batteries

Daozhong Hu,Gang Chen,Jun Tian,Ning Li,Lai Chen,Yuefeng Su,Tinglu Song,Yun Lu,Duanyun Cao,Shi Chen,Feng Wu

DOI: https://doi.org/10.1016/j.jechem.2020.12.024

IF: 13.1

2021-09-01

Journal of Energy Chemistry

Abstract:<p>The low-temperature performance of Li-ion batteries (LIBs) has important impacts on their commercial applications. Besides the metallic lithium deposition, which is regarded as one of the main failure mechanisms of the LIBs at low temperatures, the synergistic effects originating from the cathode, anode, electrolyte, and separators to the batteries are still not clear. Here, the 21700-type cylindrical batteries were evaluated at a wide range of temperatures to investigate the failure mechanism of batteries. Voltage relaxation, and the post-mortem analysis combined with the electrochemical tests, unravel that the capacity degradation of batteries at low temperature is related to the lithium plating at graphite anodes, the formation of unsatisfied solid deposited/decomposed electrolyte mixture phase on the anode, the precipitation of solvent in the electrolytes and the block of separator pores, and the uneven dissolved transition metal-ions from the cathode. We hope this finding may open up a new avenue to alleviate the capacity degradation of advanced LIBs at low temperatures and shed light on the development of outstanding low-temperature LIBs via simultaneous optimization of all the components including electrodes, electrolytes and separators.</p>

chemistry, physical,engineering, chemical, applied,energy & fuels

What problem does this paper attempt to address?

The paper primarily explores the impact of low temperatures on the cycle life of 21700 cylindrical lithium-ion batteries and their failure mechanisms. The study found that under low-temperature conditions (especially temperatures below zero), the performance of lithium-ion batteries significantly declines, specifically in the following aspects:

1. **Lithium Plating**: At low temperatures, the phenomenon of lithium plating on the graphite anode surface becomes more severe. This not only consumes the active lithium-ion inventory but also leads to the formation of lithium dendrites, thereby reducing battery capacity and posing safety risks.

2. **Solid Deposited/Decomposed Electrolyte Mixture Phase**: Low temperatures accelerate the formation of a thick and loose interface film on the anode, composed of deposition and decomposition products of the electrolyte. This interface film not only consumes active lithium ions but also increases the interfacial resistance of the anode, impairing the thermal stability of the battery.

3. **Precipitation of Solvent**: The solubility of solvents (such as ethylene carbonate) in the electrolyte decreases at low temperatures, leading to the precipitation of the solvent in the electrolyte. This clogs the pores of the separator, hindering lithium-ion transport.

4. **Dissolved Transition Metal Ions**: The uneven dissolution of transition metal ions from the cathode material, particularly the exacerbated loss of aluminum ions at low temperatures, deteriorates the structural stability of the material.

In summary, this study reveals the failure mechanisms of 21700 cylindrical lithium-ion batteries in low-temperature environments and provides a theoretical basis and technical guidance for the development of high-performance low-temperature lithium-ion batteries.