Influence mechanism of rare earth (RE) on inclusion modification in non-oriented silicon steel
Haijun Wang,Kaixuan Shao,Yuhao Niu,Jialong Qiao,Hongbo Pan,Shengtao Qiu
DOI: https://doi.org/10.1051/metal/2024074
IF: 0.9461
2024-11-02
Metallurgical Research & Technology
Abstract:Effects of rare earth (La+Ce) on inclusions in hot-rolled band of 3.0∼3.3%Si-0.8∼1.0%Al non-oriented silicon steel was studied using industrial trials, scanning electron microscope (SEM) and thermodynamic analysis. Furthermore, combining Heterogeneous Nucleation Theory with Edge-to-Edge Matching (E2EM) model, the formation mechanism of complex inclusions was also investigated. Rare earth (La+Ce) would promote the spheroidization and coarsening of inclusions, and then transform into regular and near circle morphology composite inclusions of rare earth. The low content of rare earth (21 ppm) mainly deoxidized and modified Al 2O 3 inclusions, and formed (La,Ce)AlO 3 inclusions. Increasing of rare earth (29–45 ppm) would promote the formation of (La,Ce)AlO 3-(La,Ce) 2O 2S and (La,Ce) 2O 2S inclusions, reduce the sulfide precipitation, and promote a gradual transformation of the core of composite inclusions from (La,Ce)AlO 3 to (La,Ce)AlO 3-(La,Ce) 2O 2S and (La,Ce) 2O 2S, which agreed well with the thermodynamic analysis. However, rare earth (29–45 ppm) had a weak metamorphic effect on Al 2O 3 inclusions generated by temperature drop and secondary oxidation. LaAlO 3, CeAlO 3, La 2O 2S and Ce 2O 2S could be the heterogeneous nucleation core of AlN, Al 2O 3, MgO-Al 2O 3, typical composite inclusions with (La,Ce)AlO 3 and (La,Ce) 2O 2S as the core would ultimately form.
metallurgy & metallurgical engineering