Abstract:Rapid repair and retrofit of existing infrastructures demand durable high early strength materials that not only deliver sufficient strength within a short time after placement but also significantly prolong the maintenance interval. This research paper presents the effects on the mechanical properties and durability of alccofine concrete of the addition of calcium nitrate as a non-chloride hardening accelerator (NCHA). Non-chloride accelerator with concentrations of 0.65%, 0.85% and 1.05% by weight of cement, was added to concrete mixes to test the effect on the properties of alccofine concrete which was in turn compared with the reference concrete without NCHA. With addition of accelerator, strength enhancements were observed at an early age due to rapid rate of hydration of C3A and C3S phases. Water absorption and sulphate resistance of alccofine concrete also improved with the non-chloride accelerator. A statistical tool was used to predict the experimental values of compressive strength of concrete. Response surface methodology was adopted to optimize the experimental data set in which regression equation was developed by relating response variable to input variable. This method helped to predict the experimental values within an acceptable error range. The predicted values were cross validated by employing coefficient of determination (R2) and residual sum of squares (RSS) which showed a good fit. The results of this study showed that the addition of non-chloride hardening accelerator in alccofine concrete significantly improved the mechanical properties as well as durability.
What problem does this paper attempt to address?
### Problems the Paper Aims to Solve
The paper aims to address the demand for early high-strength materials in the rapid repair and renovation of existing infrastructure. Specifically, the research focuses on enhancing the early strength and durability of concrete by adding non-chloride hardening agents (NCHA). The research objectives include:
1. **Enhancing Early Strength**: Accelerating the hydration rate of C3A and C3S phases in cement by adding non-chloride hardening agents, thereby increasing the early strength of concrete in a short period.
2. **Improving Durability**: Evaluating the effect of non-chloride hardening agents on the water absorption and sulfate resistance of concrete.
3. **Optimizing Experimental Data**: Using the response surface methodology (RSM) to optimize the experimental data set, establish regression equations to predict the compressive strength of concrete, and verify the accuracy of the predicted values.
### Research Background
Traditional concrete has low early strength, which can slow down construction progress. High early strength concrete (HESC) can achieve high strength in a short period, making it suitable for rapid track laying, precast components, and concrete engineering in cold regions. However, commonly used acceleration methods such as special cement and heat treatment have high production costs or are inconvenient for practical application. Therefore, the use of early strength agents has become one of the most cost-effective methods.
### Research Methods
1. **Material Selection**:
- Cement: Khyber brand 43-grade ordinary Portland cement.
- Aggregates: Natural river sand as fine aggregate and crushed stone as coarse aggregate.
- Alccofine: An ultra-fine mineral additive, replacing 25% of the cement.
- Non-chloride hardening agent: Master set AC 100, mainly composed of calcium nitrite.
2. **Concrete Mix Proportion**:
- Four different concrete mixtures with varying amounts of non-chloride hardening agents were prepared, with a water-cement ratio of 0.45.
- The reference concrete did not contain any non-chloride hardening agents.
3. **Testing Methods**:
- Compressive Strength: Using 150 mm cubic specimens, testing the compressive strength at 3, 7, and 28 days.
- Splitting Tensile Strength: Using 150 mm x 300 mm cylindrical specimens, testing the splitting tensile strength at 7 and 28 days.
- Flexural Strength: Using 100 mm x 100 mm x 500 mm beam specimens, testing the flexural strength at 7 and 28 days.
- Water Absorption: Using 150 mm cubic specimens, testing the water absorption at 7 and 28 days.
- Sulfate Resistance: Immersing the specimens in a 5% sodium sulfate solution, testing the mass loss and strength degradation rate after 28 days.
### Results and Discussion
1. **Compressive Strength**:
- The compressive strength of concrete with non-chloride hardening agents increased by 22.34%, 35.05%, and 29.02% at 3 days.
- The increase in compressive strength at 7 days was smaller, at 5.76%, 11.89%, and 6.95%.
- The long-term compressive strength at 28 days was slightly higher than the reference concrete.
2. **Splitting Tensile Strength**:
- The splitting tensile strength of concrete with non-chloride hardening agents increased by 9.54%, 23.32%, and 16.21% at 7 days.
3. **Flexural Strength**:
- The flexural strength of concrete with non-chloride hardening agents increased by 7.24%, 29.03%, and 26.66% at 7 days.
4. **Water Absorption**:
- The water absorption of concrete with non-chloride hardening agents decreased, indicating reduced porosity and increased density.
5. **Sulfate Resistance**:
- The mass loss and strength degradation rate of concrete with non-chloride hardening agents in the sulfate resistance test were lower, indicating enhanced erosion resistance.
### Conclusion
The study shows that adding non-chloride hardening agents can significantly improve the early strength and durability of Alccofine concrete. By optimizing experimental data using the response surface methodology, a regression equation was established to predict the compressive strength of concrete, and the predicted values matched well with the actual values. These results provide an effective material solution for the rapid repair and renovation of existing infrastructure.