Abstract:The purpose of this study is to prove the feasibility, efficiency and selectivity of lithium recovery from waste lithium-ion batteries (LIB) via sulfuric acid roasting-water leaching by thermodynamic analysis and experimental verification. The feasibility was proved by Gibbs free energy calculations and experiments. Then, the effects of H 2 SO 4 concentration, roasting temperature and roasting time were assessed on the leaching rate of valuable metals. The results indicate that the leaching efficiency of lithium increases firstly and then decreases with the increase of H 2 SO 4 concentration, roasting temperature and roasting time, more than 91 % lithium are leached under optimized experimental conditions: 50 wt% H 2 SO 4 , roasting temperature of 650°C, and roasting time of 2 h. Meanwhile, the selectivity of lithium is up to 88 % which means overwhelming majority lithium have been separated completely. In addition, the factors which cause sintering phenomenon such as high temperature and longtime roasting will change the microstructure of roasted product extremely, which is inconducive to the subsequent water leaching. The investigations of the phase conversion mechanism by thermodynamic simulation and instrumental characterization indicated that the leaching behaviors of valuable metals might be influenced by the different reaction pathways of the compounds while changing roasting conditions. The recovery process can be divided into two stages: the partial structure of LiNi x Co y Mn z O 2 was destroyed to form metal sulfates at ambient temperature and the solid phase reaction between unreacted LiNi x Co y Mn z O 2 which contained Li + in the unstable layered structure with transition metal sulfates at high temperature. The fully reduced low-valence states are mainly (NiO) 0.75 (MnO) 0.25 and CoO, and basically all Li within the crystalline LiNi x Co y Mn z O 2 was de-intercalated and transformed to soluble Li 2 SO 4 . These results further confirm the advantages of H 2 SO 4 roasting on selective Li recovery, and provide a better understanding of conversion mechanism by combining theory and experiments.

Sulfation Roasting Mechanism for Spent Lithium-Ion Battery Metal Oxides Under SO2-O2-Ar Atmosphere

Preferentially selective recovery of lithium from spent LiCoO2 by sulfation roasting of MnSO4

Selective lithium recovery from black powder of spent lithium-ion batteries via sulfation reaction: phase conversion and impurities influence

Sodium sulfite roasting for preferential lithium extraction from cathode material of spent lithium-ion batteries

A Simplified Process for Recovery of Li and Co from Spent LiCoO2 Cathode Using Al Foil As the in Situ Reductant

Study on the reduction roasting of spent LiNixCoyMnzO2 lithium-ion battery cathode materials

Selective lithium recovery from waste lithium-ion batteries by H 2 SO 4 roasting focused on process intensification and conversion mechanism

Selective lithium extraction and regeneration of LiCoO2 cathode materials from the spent lithium-ion battery

Preferentially selective extraction of lithium from spent LiCoO2 cathodes by medium-temperature carbon reduction roasting

Recovery of spent LiCoO2 lithium-ion battery via environmentally friendly pyrolysis and hydrometallurgical leaching

Recycling of valuable metals from spent lithium-ion batteries by self-supplied reductant roasting

Recycling of Li, Co from spent LiCoO2 cathode materials through a low temperature urea-assisted sulfation roasting approach

Extraction of Co and Li2CO3 from cathode materials of spent lithium-ion batteries through a combined acid-leaching and electro-deoxidation approach

Efficient recovery of lithium as Li2CO3 and cobalt as Co3O4 from spent lithium-ion batteries after leaching with p-toluene sulfonic acid

Converting spent lithium cobalt oxide battery cathode materials into high-value products via a mechanochemical extraction and thermal reduction route

Sustainable recycling of LiCoO2 cathode scrap on the basis of successive peroxymonosulfate activation and recovery of valuable metals

Recycling for Recovery of Critical Metals from LiCoO2 Cathode Material Through Methanesulfonic Acid-Citric Acid Organic Leaching System

Organics removal combined with in situ thermal-reduction for enhancing the liberation and metallurgy efficiency of LiCoO2 derived from spent lithium-ion batteries

Leaching Li from Mixed Cathode Materials of Spent Lithium-ion Batteries by Carbon Thermal Reduction

Improved recovery of lithium from spent lithium-ion batteries by reduction roasting and NaHCO3 leaching

Selective Lithium Leaching from Spent Lithium-Ion Batteries Via a Combination of Reduction Roasting and Mechanochemical Activation