Abstract:The purpose of this study is to prove the feasibility, efficiency and selectivity of lithium recovery from waste lithium-ion batteries (LIB) via sulfuric acid roasting-water leaching by thermodynamic analysis and experimental verification. The feasibility was proved by Gibbs free energy calculations and experiments. Then, the effects of H 2 SO 4 concentration, roasting temperature and roasting time were assessed on the leaching rate of valuable metals. The results indicate that the leaching efficiency of lithium increases firstly and then decreases with the increase of H 2 SO 4 concentration, roasting temperature and roasting time, more than 91 % lithium are leached under optimized experimental conditions: 50 wt% H 2 SO 4 , roasting temperature of 650°C, and roasting time of 2 h. Meanwhile, the selectivity of lithium is up to 88 % which means overwhelming majority lithium have been separated completely. In addition, the factors which cause sintering phenomenon such as high temperature and longtime roasting will change the microstructure of roasted product extremely, which is inconducive to the subsequent water leaching. The investigations of the phase conversion mechanism by thermodynamic simulation and instrumental characterization indicated that the leaching behaviors of valuable metals might be influenced by the different reaction pathways of the compounds while changing roasting conditions. The recovery process can be divided into two stages: the partial structure of LiNi x Co y Mn z O 2 was destroyed to form metal sulfates at ambient temperature and the solid phase reaction between unreacted LiNi x Co y Mn z O 2 which contained Li + in the unstable layered structure with transition metal sulfates at high temperature. The fully reduced low-valence states are mainly (NiO) 0.75 (MnO) 0.25 and CoO, and basically all Li within the crystalline LiNi x Co y Mn z O 2 was de-intercalated and transformed to soluble Li 2 SO 4 . These results further confirm the advantages of H 2 SO 4 roasting on selective Li recovery, and provide a better understanding of conversion mechanism by combining theory and experiments.

Selective lithium recovery from black powder of spent lithium-ion batteries via sulfation reaction: phase conversion and impurities influence

Removal of impurity metals as phosphates from Lithium-ion battery leachates

Selective lithium recovery from waste lithium-ion batteries by H 2 SO 4 roasting focused on process intensification and conversion mechanism

Preferentially selective recovery of lithium from spent LiCoO2 by sulfation roasting of MnSO4

Unveiling the lithium deintercalation mechanisms in spent lithium-ion batteries via sulfation roasting

Sulfation Roasting Mechanism for Spent Lithium-Ion Battery Metal Oxides Under SO2-O2-Ar Atmosphere

Selective Lithium Leaching from Spent Lithium-Ion Batteries Via a Combination of Reduction Roasting and Mechanochemical Activation

Priority recovery of lithium and effective leaching of nickel and cobalt from spent lithium-ion battery

Selective lithium recovery and integrated preparation of high-purity lithium hydroxide products from spent lithium-ion batteries

Improved recovery of lithium from spent lithium-ion batteries by reduction roasting and NaHCO3 leaching

Study on the reduction roasting of spent LiNixCoyMnzO2 lithium-ion battery cathode materials

Preferentially selective extraction of lithium from spent LiCoO2 cathodes by medium-temperature carbon reduction roasting

Preferential and efficient extraction of lithium under the combined action of reduction of herb-medicine residue and leaching of oxalic acid

Selective Recovery of Valuable Metals from Spent Lithium-Ion Batteries – Process Development and Kinetics Evaluation

Thermodynamic and experimental analysis of lithium selectively recovery from spent lithium-ion batteries by in-situ carbothermal reduction

Leaching Li from Mixed Cathode Materials of Spent Lithium-ion Batteries by Carbon Thermal Reduction

Recovering valuable metals from LiNixCoyMn1-x-yO2 cathode materials of spent lithium ion batteries via a combination of reduction roasting and stepwise leaching

Chemical speciation changes of an all-solid-state lithium-ion battery caused by roasting determined by sequential acid leaching

High-efficiency recovery of valuable metals from spent lithium-ion batteries: Optimization of SO 2 pressure leaching and selective extraction of trace impurities

Recycling of valuable metals from spent lithium-ion batteries by self-supplied reductant roasting

Improved recovery of valuable metals from spent lithium-ion batteries by efficient reduction roasting and facile acid leaching.