Abstract:A high-temperature, high-cycle fatigue test was conducted on a nickel-based single-crystal superalloy with a pore structure. Optical and scanning electron microscopy were utilized to examine the crack propagation paths and fatigue fracture surfaces at the macro and micro scales. The analysis of crack initiation and propagation related to the pore structure facilitated the development of a crack shape factor reflecting these distinct fracture behaviors. Predictions about the high-cycle fatigue stress experienced by the specimen were made, accompanied by an error analysis, providing critical insights for precise stress calculations and structural optimization in engine blade design. The results reveal that high-cycle fatigue cracks originate from corner cracks at pore edges, with the initial propagation displaying smooth crystallographic plane features. Subsequent stages show clear fatigue arc patterns in the propagation zones. The fracture surface exhibits the significant layering of oxide layers, primarily composed of NiO, with traces of CoO displaying columnar growth. AL2O3 is predominantly found at the interfaces between the matrix and oxide layers. Short and straight dislocations near the oxide layers and within the matrix suggest that dislocation multiplication and planar slip dominate the slip mechanisms in this alloy. The orientation of the fracture surface is mainly perpendicular to the load direction, with minor inclined facets in localized areas. Correlations were established between the plastic zone dimensions at the crack tips and the corresponding fatigue stresses. Without grain boundaries in single-crystal alloys, these dimensions are easily derived as parameters for fatigue stress analysis. The selected crack shape factor, "elliptical corner crack at pore edges", captures the initiation and propagation traits relevant to porous structures. Subsequent calculations, accounting for the impact of oxide layers on stress assessments, indicated an error ratio ranging from 1.00 to 1.21 compared to nominal stress values.

The origin of fatigue fracture in single-crystal silicon

A reaction-layer mechanism for the delayed failure of micron-scale polycrystalline silicon structural films subjected to high-cycle fatigue loading

Influence of Strain Amplitude on Low-Cycle Fatigue Behaviors of a Fourth-Generation Ni-Based Single-Crystal Superalloy at 980 °C

Fatigue fracture mechanism of sputtered AlSi alloy film by pulsating-tension cyclic loading testing

Low Amplitude Cyclic Deformation Behavior of Single Crystalline Silicon

Fatigue fracture mechanism of amorphous materials from a density-based coarse-grained model

Eliciting stable nanoscale fracture in single-crystal silicon

Damage accumulation during high temperature fatigue of Ti/SiCf metal matrix composites under different stress amplitudes

Damage accumulation during high temperature fatigue of Ti/SiC$_f$ metal matrix composites under different stress amplitudes

Fatigue behaviour analysis of thermal cyclic loading for through-silicon via structures based on backstress stored energy density

High temperature in-situ SEM observation and crystal plasticity simulation on fretting fatigue of Ni-based single crystal superalloys

Atomistic Simulations of Dislocation Activity in Si Nanofibers in Al-Si Eutectics

High-Cycle Fatigue Fracture Behavior and Stress Prediction of Ni-Based Single-Crystal Superalloy with Film Cooling Hole Drilled Using Femtosecond Laser

Fracture of a silicon nanowire at ultra-large elastic strain

Fatigue Fracture Mechanism of a Nickel-Based Single Crystal Superalloy with Partially Recrystallized Grains at 550 C by In Situ SEM Studies

Integrating atomistics and experiments in gaining deeper insights into fatigue crack propagation in silver

The Tensile Effect on Crack Formation in Single Crystal Silicon Irradiated by Intense Pulsed Ion Beam

A Microscopic Tem Study Of The Defect Layers In Cast-Mono Crystalline Silicon Wafers Induced By Diamond-Wire Sawing

In-situ SEM study of slip-controlled short-crack growth in single-crystal nickel superalloy

Crystallographic analysis for fatigue small crack growth behaviors of a nickel-based single crystal by in situ SEM observation

Simulation Of Near-Crack-Tip Strain Fields On Single-Crystal Silicon Wafer