Effect of magnetite addition to ilmenite on hydrogen-rich reduction of its oxidized powder
Furong Chen,Wei Lv,Gangwei Zhou,Zhuoliang Liu,Mansheng Chu,Xuewei Lv
DOI: https://doi.org/10.1016/j.ijhydene.2023.05.363
IF: 7.2
2023-06-18
International Journal of Hydrogen Energy
Abstract:In this study, the oxidation powder sample of ilmenite concentrate with 15% magnetite concentrate was prepared, and the subsequent isothermal reduction was investigated at temperatures in the range of 950–1050 °C with CO, H 2 , and their mixtures. The hydrogen-rich atmosphere, magnetite effect, apparent activation energy, and micromorphology of the reduced samples were investigated. The results indicated that the mass loss of the raw sample in the reduction process exhibited a similar tendency to that of the preoxidized ilmenite concentrate, although the addition of the magnetite concentrate increased the total mass loss. The influence of Fe 2 O 3 , which is produced by the oxidation of magnetite, on the mass-change ratio in the reduction process is separated and drawn novelty. The interaction between the magnetite and ilmenite concentrates in the oxidation process did not exhibit an apparent hindering effect following the hydrogen-rich reduction of the raw sample powder. The reducing atmosphere had a slight influence on the average apparent activation energy. The average apparent activation energies of the reduction of the raw sample were 55.34, 53.54, 52.78, 59.14, and 53.85 kJ/mol when the reducing atmosphere was CO, H 2 /CO = 0.4, H 2 /CO = 1, H 2 /CO = 2.5, and H 2, respectively. Furthermore, the change in micromorphology of the reduced sample with the hydrogen-rich content in the reduction atmosphere is also discussed.
energy & fuels,electrochemistry,chemistry, physical