Non-isothermal Reduction Kinetics of Iron During Vacuum Carbothermal Reduction of Ilmenite Concentrate

Huang Run,Lv Xiaodong,Wu Qinghui,Wu Qinzhi,Zhang Jinzhu

DOI: https://doi.org/10.1007/s11663-019-01529-9

2019-02-06

Metallurgical and Materials Transactions B

Abstract:<h3 class="a-plus-plus">Abstract</h3> <p class="a-plus-plus">The non-isothermal reduction kinetics and mechanism of iron during vacuum carbothermal reduction of ilmenite concentrate were investigated by X-ray diffraction, backscattered electron imaging, and energy-dispersive X-ray spectroscopy at temperatures from 1273 K to 1673 K (1000 °C to 1400 °C). The pressure dropped and the increasing trend of mass loss and metallization ratios slowed down when the temperature was higher than 1573 K (1300 °C). The reaction products were iron, Ti<sub class="a-plus-plus">2</sub>O<sub class="a-plus-plus">3</sub>, and silicate. Iron was mainly obtained by carbothermal reduction of FeTiO<sub class="a-plus-plus">3</sub> and FeTi<sub class="a-plus-plus">2</sub>O<sub class="a-plus-plus">5</sub>. The irons continued to nucleate, aggregate, and grow during the reduction process. Comprehensive consideration of Šatava–Šesták method and Coats–Redfern method, the apparent activation energy of the reduction process was 587.4 ± 2.98 kJ/mol, and the forms of both integral and differential for the mechanism function were <em class="a-plus-plus">G</em>(<em class="a-plus-plus">a</em>)<em class="a-plus-plus">=</em> [(1<em class="a-plus-plus">−a</em>)<sup class="a-plus-plus"><em class="a-plus-plus">−</em>1/3</sup><em class="a-plus-plus">−</em>1]<sup class="a-plus-plus">2</sup> and <em class="a-plus-plus">f</em>(<em class="a-plus-plus">a</em>) <em class="a-plus-plus">=</em> 3/2(1<em class="a-plus-plus">−a</em>)<sup class="a-plus-plus">4/3</sup>[(1−<em class="a-plus-plus">a</em>)<em class="a-plus-plus">−</em><sup class="a-plus-plus">1/3</sup><em class="a-plus-plus">−</em>1]<sup class="a-plus-plus"><em class="a-plus-plus">−</em>1</sup>, respectively.</p>

materials science, multidisciplinary,metallurgy & metallurgical engineering