High mechanical performance alumina-reinforced aluminum nanocomposite metal foam produced by powder metallurgy: fabrication, microstructure characterization, and mechanical properties

Hamid Oveisi,Toktam Geramipour

DOI: https://doi.org/10.1088/2053-1591/ab608b

IF: 2.025

2020-01-06

Materials Research Express

Abstract:In this research, alumina-reinforced aluminum nanocomposite foams with high compressive performancewere produced using the powder compact melting (PCM) process and CaCO 3 foaming agent. The contentof Al 2 O 3 nanoparticles, with sizes smaller than 80 nm, varied between 0–15 wt%. Aluminum, Al 2 O3 , and CaCO 3 powders were mixed and compacted to dense precursors with 318 MPa stress. Finally,foam samples were fabricated by heating up the precursors at 1000 °C for 10 min. A range of porosityvalues was achieved between 34% to 43% for different combinations of aluminum matrix and aluminareinforcement phase. The crystallite size of the alumina reinforcement phase in Al-3 wt% alumina andAl-15 wt% alumina composite foam was estimated as 23.51 nm and 23.24 nm while the crystallite sizeof the aluminum matrix was determined as 15.72 nm and 15.44 nm for the same samples. The FieldEmission Scanning Electron Microscope (FESEM) ...

materials science, multidisciplinary