Nanoindentation response of interphase precipitation in a Nb microalloyed steel

Xuefeng Liu,Yong Yang,Tao Jia,Xiaoming Zhang,Zhaodong Wang
DOI: https://doi.org/10.1080/02670836.2019.1711337
IF: 1.8
2020-01-13
Materials Science and Technology
Abstract:In this work, dedicated isothermal transformation studies were performed in a Fe–C–Mn–Nb alloy to obtain two types of precipitate morphology embedded in a similar ferritic matrix. Nano-hardness of individual ferrite grain was measured by using an in situ nano-mechanical tester. The peak of nano-hardness distribution from interphase and dispersed precipitate strengthened ferrite corresponds to the nano-hardness range of 2.6–2.8 and 2.5–2.6 GPa, respectively. A wider spread of nano-hardness from interphase precipitate strengthened ferrite was observed and rationalised by considering the variation in inter-particle spacing on slip planes. The 'pop-ins' on the load-depth curve was not able to be correlated with the morphology of a precipitate.
materials science, multidisciplinary,metallurgy & metallurgical engineering
What problem does this paper attempt to address?