Precipitation behavior in G-phase strengthened ferritic stainless steels

Mujin Yang,Daniel J.M. King,Ivan Povstugar,Yuren Wen,Junhua Luan,Bernd Kuhn,Zengbao Jiao,Cuiping Wang,M.R. Wenman,Xingjun Liu,Daniel.J.M. King
DOI: https://doi.org/10.1016/j.actamat.2020.116542
IF: 9.4
2021-02-01
Acta Materialia
Abstract:<p>A series of G-phase strengthened ferritic stainless steels Fe-20Cr-3Ni-3Si-X (X=2Mn, 1Mn-2Ti, 1Mn-2Nb and 1Mn-2Ta) are characterized after aging using experimental (microhardness, TEM and APT) and theoretical (DFT) techniques. The results indicate that the Ni<sub>16</sub>Mn<sub>6</sub>Si<sub>7</sub> G-phase shows sluggish precipitation during aging treatment. This was attributed to the small difference in the enthalpy of formation between the Ni<sub>16</sub>Mn<sub>6</sub>Si<sub>7</sub> G- and BCC phase and the requirement of high Ni:Fe ratio. A superfine Ni<sub>16</sub>Ti<sub>6</sub>Si<sub>7</sub> G-phase was found to precipitate as a core accompanied with an "envelope" of Fe<sub>2</sub>TiSi-L2<sub>1</sub> Heusler phase during early aging (≤24 h) in the Ti containing alloy. This morphology is predicted to occur due to early Ni clustering in ferrite and a negative Ni concentration gradient away from the cluster that favors Fe<sub>2</sub>TiSi formation. The G-phases show only particle coarsening without obvious chemical composition evolution for further aging up to 96 h. A prominent hardness increase of 100-275 HV was also observed during aging. These findings provide valuable insight into methods for precipitating low lattice mismatch silicide phases for the development of future high strength steels.</p>
materials science, multidisciplinary,metallurgy & metallurgical engineering
What problem does this paper attempt to address?