Abstract:A tribo-oxide layer is generally formed on the contact surfaces during the high temperature friction and wear process, which significantly influences the tribological properties of the materials. In this work, the evolution mechanism of tribo-oxide layer for nickel-based superalloy was studied. High temperature sliding wear tests were performed at the different sliding time from 1 min to 60 min for nickel-based superalloy (Ni-16Cr-13Co-4Mo) against a Si3N4 ball at 800°C under ambient environment. Morphology and chemical composition of the worn surface and wear debris were investigated using a Scanning electron microscope (SEM), X-Ray diffraction (XRD) and Raman spectroscope. The cross-sectional microstructure and element distribution of the worn surface and untested area were characterized by EDS mapping attached to the SEM. Results show that the evolution of tribo-oxide layer can be divided into three stages. The first stage is characterized by the formation of a mixed oxide layer due to the preferential oxidation of Cr, Al and Ti in the preheating and temperature holding process. In the second stage, a dense tribo-oxide layer is formed by compacting and sintering the wear debris retained on the worn surface accompanying the inner oxidation of the dissolved γ' phase and Cr in the alloy. In the third stage, the oxide layer with a layered structure formed with an outmost layer composed of mixed oxides with a spinel structure and an inner oxide layer played a barrier role to prevent further oxidation of the substrate. It is speculated that the change in the structure of spinel oxides at high temperature from order to disorder led to the decrease in shear stress, eventually resulted in the reduction of friction coefficient and the low wear rate.

High-Temperature Friction and Wear Features of Nickel-Based Single Crystal Superalloy

Study on nanoscale friction and wear mechanism of nickel-based single crystal superalloy by molecular dynamics simulations

Tribological Behavior of a Shot-Peened Nickel-Based Single Crystal Superalloy at High Temperature

Temperature Effects on Deformation Substructures and Mechanisms of a Ni-based Single Crystal Superalloy

The evolution mechanism of tribo-oxide layer during high temperature dry sliding wear for nickel-based superalloy

Tribo-induced surface structure of Nickel-based superalloy at elevated temperature

Creep Behavior and Deformation Mechanism of a Third-Generation Single Crystal Ni-Based Superalloy at 980 °C

Thermomechanical Fatigue of Nickel-Based Single-Crystal Superalloys

In-situ SEM study on fatigue crack behavior of a nickel-based single crystal alloy at 950 °C and 1050 °C

Fatigue Fracture Mechanism of a Nickel-Based Single Crystal Superalloy with Partially Recrystallized Grains at 550 C by In Situ SEM Studies

A novel wear-resistant Ni-based superalloy via high Cr-induced subsurface nanotwins and heterogeneous composite glaze layer at elevated temperatures

Fretting fatigue damage mechanism of Nickel-based single crystal superalloys at high temperature

Study on force and temperature characteristics of micro-grinding nickel-based single-crystal superalloy

Molecular Dynamics Study on Nano-Friction and Wear Mechanism of Nickel-Based Polycrystalline Superalloy Coating

Temperature Dependence of High-Cycle Fatigue Behavior of a Ni-Base Single Crystal Superalloy

Influence of Residual Stress on the High-Temperature Tribological Performance of Nickel-Based Superalloy

Effect of Local Recrystallized Grains on the Low Cycle Fatigue Behavior of a Nickel-Based Single Crystal Superalloy

Temperature effect on the low cycle fatigue behavior of a directionally solidified nickel-base superalloy

Temperature Effect on Low-Cycle Fatigue Behavior of Nickel-Based Single Crystalline Superalloy

High temperature in-situ SEM observation and crystal plasticity simulation on fretting fatigue of Ni-based single crystal superalloys

Atomic behavior of nickel-based single crystal superalloy during heat treatment process based on molecular dynamics