Optical Performance, Thermal Stability, and Failure Analysis of the WN x -Si 3 N 4 Multilayer Solar Selective Absorbing Coatings
Binghui Sun,Lei Wang,Ying Sun,Jie Ren,Yingxin Yang,Huan Liu,Dongdong Liang,Aoyu Li,Cong Wang
DOI: https://doi.org/10.1021/acsaem.1c03373
IF: 6.4
2022-01-19
ACS Applied Energy Materials
Abstract:The development of high-temperature-tolerance solar selective absorbing coatings (SSACs) is beneficial to improve the conversion efficiency of concentrated solar power. In the present work, a TiN/Mo/WN x -Si3N4 bilayer/SiO2 cermet-based SSAC was developed, which was deposited on different substrates by magnetron sputtering. The designed WN x -Si3N4 SSAC exhibits a high solar absorptivity of 0.952, accompanied by a relatively low emissivity of 0.059 at 25 °C and 0.134 deduced at 600 °C. Moreover, the WN x -Si3N4 SSAC deposited on a stainless-steel (SS) substrate shows great thermal stability at 650 °C in vacuum. The solar absorptivity shows a slight decrease from 0.952 to 0.939 and the emissivity at 25 °C decreases from 0.059 to 0.045 after being annealed at 650 °C in vacuum. Furthermore, when being annealed at 700 °C in vacuum, the WN x -Si3N4 SSAC deposited on the quartz glass substrate still keeps stable, but the coating on the SS substrate is dramatically destroyed. A comprehensive failure analysis was conducted utilizing FT-IR, SEM, Raman, and XPS characterizations. The degradation of the WN x -Si3N4 SSAC deposited on the SS substrate at 700 °C is caused by the severe elemental diffusion between the absorbing layers and the antireflection layer. Moreover, the cracks induced by the thermal stress provide rapid channels for elemental diffusion.
materials science, multidisciplinary,chemistry, physical,energy & fuels