THERMAL STABILITY OF Mo-SiO2 SOLAR SELECTIVE COATINGS AT HIGH TEMPERATURES IN AIR

Qirui Wei,Jian Wang,Dejie Li,Zhiqiang Yin

DOI: https://doi.org/10.19912/j.0254-0096.2011.08.011

2011-01-01

Abstract:Mo-SiO 2 multilayer solar selective coatings were deposited by magnetron sputtering technique. The samples were annealed in atmosphere at different temperatures ranging from 500°C to 700°C for 1hour. The reflectance in the wavelength region of 0.34-25μm of the as-deposited and annealed samples were measured with UV-VIS-NIR and FT-IR spectrometers. The solar absorptance (α) and thermal emittance (ε) of as-deposited coatings were 0.95 and 0.093, respectively. The reflectance was nearly the same after anneal in air at 500°C and 600°C for 1hour. The spectra selectivity of coating deteriorated after annealing in air at 700°C for 1hour, whose α and ε were changed to 0.91 and 0.6, respectively. Then Mo, SiO 2 single layer and Mo/SiO 2 tandem layers were deposited with the same process and annealed in air at different temperatures for 1hour. The surface morphology of as-deposited and annealed films were investigated with scanning electronic microscopy. The annealed films became rough, and cracks and peelings appeared, and was the main reason of spectra selectivity deterioration.