Abstract:A Mg-Gd-Y-Zn-Zr magnesium alloy with different initial states was extruded under different extrusion parameters. The effect of solution treatment and extrusion parameters on the microstructure, texture and mechanical properties were analyzed in detail, and the abnormal texture formation and strengthening mechanism was revealed. When extruded at low temperature and small extrusion ratio, the bimodal microstructure consisting of fine dynamically recrystallized grains and coarse deformed grains occurred both in the as-cast alloy and solution-treated alloy. When the extrusion temperature and extrusion ratio were increased, the amount and size of dynamically recrystallized grains increased and the grain size of the solution-treated alloy showed higher growth rate. Furthermore, an abnormal texture with <0001> parallel with extrusion direction developed due to the occurrence of non-basal slip and continuous dynamic recrystallization. This could be enhanced by solution treatment, high temperature, and large extrusion ratio. Both the as-cast alloy and solution-treated alloy exhibited the highest tensile strength after extrusion at 300 °C with an extrusion ratio of 9. Grain refinement was the main strengthening mechanism utilized in both the as-cast alloy and the solution-treated alloy. Work hardening played an important role in the sample extruded at low temperature and small extrusion ratio, with the highest contribution of about 33 MPa after extrusion at 300 °C with an extrusion ratio of 9. Texture strengthening contributed more in the sample extruded at high temperature and large extrusion ratio, but no more than 24.1 MPa. Solution strengthening was another strengthening mechanism in the extruded as-cast alloy, especially at high temperature and large extrusion ratio (no more than 9 MPa).

Texture Analysis on the AZ31 Magnesium Alloy Using Neutron Diffraction Method

STRAIN-INDUCED TEXTURE DEVELOPMENT IN THE MAGNESIUM ALLOY AZ31

Texture and Its Effect on Mechanical Properties of AZ31 Magnesium Alloy

Textures in Multi-Directional Forged Mg by Neutron Diffraction

Polycrystalline Behavior Analysis of Extruded Magnesium Alloy AZ31

Investigation on the anisotropy of mechanical properties along different orientations of an AZ31 hot-extrusion bar

Quantitative analysis of the deformation modes and cracking modes during low-cycle fatigue of a rolled AZ31B magnesium alloy: The influence of texture

Effect of Al Concentration on Basal Texture Formation Behavior of AZ-Series Magnesium Alloys during High-Temperature Deformation

Effect of texture types on microstructure evolution and mechanical properties of AZ31 magnesium alloy undergoing uniaxial tension deformation at room temperature

Thermal Stability of Different Texture Components in Extruded Mg–3Al–1Zn Alloy

A novel method of experimental determination of grain stresses and critical resolved shear stresses for slip and twin systems in a magnesium alloy

Understanding the weakening of texture in multiaxial forged ultrafine-grained strong and ductile Mg-2Zn-2Gd alloy

Role of Crystal Orientation in the Dynamic Strength of Magnesium Alloy AZ31B

Study of Effects of Initial Texture on the Microstructure and Texture for Hot Rolled AZ31 Mg Alloy Sheet Using EBSD

Evolution of Microstructure and Texture During Uniaxial Compression of Cast AZ31Mg Alloy at Elevated Temperatures

Analysis of Abnormal Texture Formation and Strengthening Mechanism in an Extruded Mg-Gd-Y-Zn-Zr Alloy

Microstructural evolution of AZ31 Mg alloy with surface mechanical attrition treatment: Grain and texture gradient

Study of the microstructure, texture and tensile properties of as-extruded AZ91 magnesium alloy

Modeling the correlation between texture characteristics and tensile properties of AZ31 magnesium alloy based on the artificial neural networks

Microtexture Evolution Via Deformation Twinning and Slip During Compression of Magnesium Alloy AZ31

Texture property and weakening mechanism of Mg-3Al-1Zn alloy by interactive alternating forward extrusion