Abstract:The surface mechanical attrition treatment was taken to fabricate the gradient structure in AZ31 magnesium alloy sheet. Microstructural investigations demonstrate the formation of dual gradients with respect to grain size and orientation, where the microstructural sizes decreased from several microns to about 200 nm from center area to treated surface, while the c-axis gradually inclined from being vertical to treated plane towards parallel with it. According to tensile results, the gradient structured sample has yield strength of 305 MPa in average, which is increased by about 4 times when compared with its coarse-grained counterpart. Meanwhile, contrary to quickly failure after necking in most traditional magnesium alloys, the failure process of gradient structure appears more gently, which makes it has 6.5% uniform elongation but 11.5% total elongation. The further comparative tensile tests for separated gradient layers and corresponding cores demonstrate that the gradient structured sample has higher elongation either in uniform or in post-uniform stages. In order to elucidate the relationship between mechanical properties and deformation mechanisms for this dual gradient structure, the repeated stress relaxation tests and pole figure examinations via X-ray diffraction were conducted in constituent gradient layer and corresponding core, as well as gradient structured sample. The results show that the pyramidal dislocations in dual gradient structure are activated through the whole thickness of sample. Together with the contribution of grain-size gradient, more dislocations are activated in dual gradient structure under tensile loading, which results in stronger strain hardening and hence higher tensile ductility.

Microstructural evolution of AZ31 Mg alloy with surface mechanical attrition treatment: Grain and texture gradient

Strain-induced Refinement and Thermal Stability of a Nanocrystalline Steel Produced by Surface Mechanical Attritiontreatment

Strain Hardening and Tensile Behaviors of Gradient Structure Mg Alloys with Different Orientation Relationships

High-strength GWZ1031K alloy with gradient structure induced by surface mechanical attrition treatment

Microstructure Evolution and Mechanical Properties of an Mg–Gd Alloy Subjected to Surface Mechanical Attrition Treatment

Surface Nanocrystallization of Mg-3 Wt.% Li-6 Wt.% Al Alloy by Surface Mechanical Attrition Treatment

Effects of strain rate on the low cycle fatigue behavior of AZ31B magnesium alloy processed by SMAT

A Coupled EBSD/TEM Analysis of the Microstructure Evolution of a Gradient Nanostructured Ferritic/Martensitic Steel Subjected to Surface Mechanical Attrition Treatment

Effect of Surface Mechanical Attrition Treatment on Biodegradable Mg-1Ca Alloy.

Strength and Ductility with Dual Grain-Size and Texture Gradients in AZ31 Mg Alloy

A New Approach of a Gradient Nanograined Surface Layer for Mg-3Al-1Zn Alloy Induced by SMRGT

Mechanical Properties and Deformation Mechanism of Mg-Al-Zn Alloy with Gradient Microstructure in Grain Size and Orientation

Effect of Surface Mechanical Attrition Treatment on Micro-mechanical Properties of ZrCuAlNi Bulk Metallic Glass

Effect of surface mechanical attrition treatment on the microstructure of cobalt–chromium–molybdenum biomedical alloy

Microstructure and Thermal Stability of Bulk Nanocrystalline Alloys Produced by Surface Mechanical Attrition Treatment

Microstructure and Texture Evolution During Friction Stir Processing of Az31 Mg Alloy

Surface Characteristics and Fatigue Behavior of Gradient Nano-Structured Magnesium Alloy

Wear Behavior of Nanocrystalline Structured Magnesium Alloy Induced by Surface Mechanical Attrition Treatment

Influence of Microstructural Evolution on Mechanical Behaviour of Az31 Alloy Sheet Processed by Flat Extrusion Container

Measurement of Microstructural Parameters of Nanocrystalline Fe–30 Wt.%ni Alloy Produced by Surface Mechanical Attrition Treatment

Precipitation Behavior of Bulk Nanocrystalline GW103K Alloy Induced by Surface Mechanical Attrition Treatment