Abstract:In this study, a high-performance Mg–8Gd–2Y–1Zn–6Li (wt%) alloy having a TYS of 202 ± 2.6 MPa, UTS of 243 ± 2.1 MPa and EL of 10.7 ± 2.3% was successfully fabricated by casting, heat treatment and hot extrusion. The effects of intermetallic compounds on microstructure and mechanical properties were deeply investigated. The results show that the studied alloy consists of coarse deformed α-Mg grains with (0001) basal texture, fine recrystallized β-Li grains with (002) texture and three Mg3RE phase variants, which are bulk Mg3RE phase with a size range of 10–30 µm, spot Mg3RE phase with a size range of 1–2 µm and spherical Mg3RE phase with a size range of 0.3–1 µm, respectively. The spherical Mg3RE phase has a strong dispersion strengthening effect, while the bulk Mg3RE phase acts as crack resources and deteriorates the ductility. A novel island-like <math>β1R</math> phase (FCC, a = 0.78 nm) is found for the first time in the Mg-Gd-Li based alloys. It has a coherent <math>(1̅12)β1R</math>//<math>(101̅0)α</math> interface at the broad facet and a semi-coherent <math>(1̅11)β1R</math>//<math>(112̅0)α</math> interface at the end facet. The <math>β1R</math> phase transforms from <math>βH</math> phase at the semi-coherent interface by atomic shear of RE and Mg atoms. The <math>β1R</math> phase provides a significant precipitation strengthening effect to the studied alloy, while the dissolution of <math>β1R</math> phase results in the age-softening phenomenon. The high-performance of the studied alloy is mainly attributed to the α/β duplex structure, three Mg3RE phase variants, and <math>β1R</math> phase.

Strength and ductility improvement in a heterostructured Mg-Gd-Y alloy with inversely-gradient hardness distribution

Effects of solid solution and aging process on microstructure and mechanical properties of Mg-Gd-Y alloy

Investigations on Microstructure and Mechanical Properties of Cast Mg-Gd-Y-Zn-Zr-Nd Alloy

An alternating ageing-annealing process for enhancing strength and ductility of a Mg-Gd-Y-Zn-Zr alloy

Excellent isotropic mechanical properties of directed energy deposited Mg-Gd-Y-Zr alloys via establishing homogeneous equiaxed grains embedded with dispersed nano-precipitation

High-strength GWZ1031K alloy with gradient structure induced by surface mechanical attrition treatment

Preparation of high-performance Mg-Gd-Y-Mn-Sc alloy by heat treatment and extrusion

Microstructure and Mechanical Properties of Mg-Xy-1.5mm-0.4zr Alloys

Strengthening of Mg Alloy with Multiple RE Elements with Ag and Zn Doping via Heat Treatment

Microstructure Evolution and Mechanical Properties of Mg-7Gd-3Y-1Nd-1Zn-0.5Zr Alloy

High Performance Mg Alloy with Designed Microstructure and Phases

Deformation modes and fracture behaviors of peak-aged Mg-Gd-Y alloys with different grain structures

Tailoring strength and ductility of Mg97Y2Zn1 alloy through the architecture of heterogeneous lamellar structure by large-ratio hot extrusion

The Research of Microstructure and Mechanical Properties of Mg–7Gd–3Y–1Nd–0.5Zn–0.5Zr (wt%) Alloy

Tuning texture and precipitation using Y/Gd atomic ratio in iso-concentration Mg–Y–Gd–Ag–Zr extruded alloys

Microstructure Evolution and Mechanical Properties of Mg-7Gd-3Y-1Nd-2Zn-0.5Zr Alloy During Two-Step Homogenization Heat Treatment

Microstructural Evolution and Mechanical Properties of Mg-5y-5gd-Xnd-0.5zr Magnesium Alloys at Different States

High strength and high ductility achieved in a heterogeneous lamella-structured magnesium alloy

Microstructures and mechanical properties of as-extruded Mg–8Gd–2Y–1Zn–6Li alloy

Revealing precipitation behavior and mechanical response of wire-arc directed energy deposited Mg-Gd-Y-Zr alloy by tailoring aging procedures

Enhanced strength-ductility synergy and activation of non-basal slip in as-extruded Mg–Zn–Ca alloy via heterostructure