High Machinability of Plasma-Nitrided HPM80 Dies at 673K by PCD-Tools for Hot Mold-Stamping

Tatsuhiko Aizawa,Hiroshi Morita,Tatsuya Fukuda

DOI: https://doi.org/10.1016/j.promfg.2020.04.223

2020-01-01

Procedia Manufacturing

Abstract:HPM80 had been utilized as one of the martensitic stainless steel mold and die substrates for stamping. In particular, HPM80 mold was often used as hot-stamping molds for oxide glasses and optical polymers to fabricate the optical elements and DOE (Diffractive Optical Elements) with the aid of NiP (Nickel Phosphate) and NiWP (Nickel-Tungsten Phosphate) coatings. These machinable amorphous coatings were indispensable to cut and finish the tailored micro textures for DOE since HPM80 was difficult or nearly impossible to be finished by using the PCD (Poly-Crystal Diamond)-chipped tools. However, those coatings were fragile above 473 K; the original HPM80 must be modified to be fine machinable even by the diamond-chipped and coated tools for fine finishing to mirror-polished die surfaces with far less damage to cutting tools. These HPM80 substrates were plasma nitrided at 673 K under the nitrogen and hydrogen mixed gas flow to form the high content nitrogen super-saturated layer. Precise machinability experiment was performed with the use of the PCD coated WC (Co) tools to investigate the machinability of these nitrogen supersaturated HPM80 substrates. Two-phase fine-grained layer with higher nitrogen solute content than 2 mass% was machined in the ductile mode with adaptively high quality to shaping and finishing the mold die surface for stamping. Through the hardness testing, this nitrogen super-saturated die surface had higher hardness than 1400 HV; it had sufficient durability for long-term stamping operations. Finally, the turning test was employed to demonstrate that this nitrogen supersaturated HPM80 layer with the thickness of 40μm was machined with high quality to form the mirror-polished surface.

What problem does this paper attempt to address?

The problem that this paper attempts to solve is that at high temperatures (above 473 K), the traditional HPM80 mold material is difficult to be finely machined and polished by conventional diamond - coated tools, especially when manufacturing optical elements and diffractive optical elements (DOE). To solve this problem, the paper proposes a low - temperature plasma nitriding technology to improve the machinability of HPM80 mold material at 673 K. Specifically, this technology aims to form a supersaturated layer with high nitrogen content, thereby increasing the hardness and wear resistance of the material while maintaining good machinability for high - precision machining with WC(Co) tools coated with polycrystalline diamond (PCD).

### Main problems:
1. **Machining difficulties of traditional HPM80 mold material**:
- The HPM80 mold material is difficult to be finely machined and polished by conventional diamond - coated tools at high temperatures (above 473 K).
- Although traditional NiP and NiWP coatings can provide good machining performance at lower temperatures, they become brittle at high temperatures, affecting the service life of the mold and production efficiency.

2. **Application of low - temperature plasma nitriding technology**:
- Through the low - temperature plasma nitriding technology, a supersaturated layer with high nitrogen content is formed on the surface of HPM80 to increase the hardness and wear resistance of the material.
- Research on the influence of the nitriding layer on the machinability of HPM80 mold material, especially its performance when machined with PCD - coated WC(Co) tools.

### Goals:
- **Improve the machinability of HPM80 mold material**: Through the low - temperature plasma nitriding technology, enable the HPM80 mold material to be high - precision machined and polished by diamond - coated tools even at high temperatures.
- **Extend the mold life**: Increase the hardness and wear resistance of the nitriding layer, reduce tool wear, and extend the service life of the mold.
- **Optimize the machining process**: Research the microstructure and mechanical properties of the nitriding layer, optimize machining parameters, and achieve high - quality mirror - surface machining.

Through these studies, the paper hopes to provide new technologies and methods for the efficient and high - quality production of optical elements and diffractive optical elements.