Abstract:Superior performance drilling seal materials can significantly enhance coal mine gas extraction efficiency. In order to enhance the material properties, nano-SiO2, sodium silicate and styrene-acrylic emulsion are selected to optimize the pore structure and strength of the material. The results show that pores in the unmodified cement-based sealing material are mostly mesoporous, accounting for 95.44%, microporous is 4.56%. Synergistic effect of sodium silicate and SiO2 increased the proportion of microporous to 10.62%, but the total porosity is higher than that of ordinary sealing materials. SiO2 and styrene-acrylic emulsion greatly reduce the pore volume of the material. The pore volume decreases from 0.09418 cc/g to 0.05621 cc/g, and the microporous increases to 16.67%. The fractal dimensions D1 and D2 decreased by 2.73% and 3.84%, indicating that the pore surface roughness increased and the pore structure became more complicated. This paper is of great significance for improving the efficiency of gas mining.
What problem does this paper attempt to address?
The problem that this paper attempts to solve is to improve the performance of coal mine drilling sealing materials in order to significantly enhance the extraction efficiency of coal mine gas. Specifically, the research optimizes the pore structure and strength of the sealing materials by selecting nano - silica (nano - SiO_2), sodium silicate and styrene - acrylic emulsion. The application of these materials aims to reduce the porosity of the materials, optimize the pore structure, thereby increasing the compactness and strength of the sealing materials, and further improving the gas extraction efficiency.
### Research Background
Coal - bed methane is an unconventional natural gas resource associated with coal. Its calorific value is comparable to that of natural gas and is widely used in transportation, chemical industry, power generation and residential life and other fields. The extraction of coal - bed methane can not only reduce the risk of gas outburst and greenhouse effect, but also obtain clean energy and improve production efficiency. However, the micropore characteristics, low permeability and high adsorption characteristics of coal seams and the performance of sealing materials are two important factors limiting the efficient and rapid extraction of coal mine gas. With the application of hydraulic fracturing, coal seam water injection and coal seam reflection techniques, the coal seam problems have been solved, and the influence of sealing materials on gas drainage efficiency has become more and more significant.
### Solution
In order to improve the performance of sealing materials, the researchers selected nano - silica (nano - SiO_2), sodium silicate and styrene - acrylic emulsion as modifiers, and evaluated the pore structure and fractal dimension of the modified sealing materials by experimental methods (such as liquid nitrogen adsorption and scanning electron microscopy). The research results show that the pore volume of the modified materials is significantly reduced, the proportion of micropores is increased, the pore surface roughness is increased, and the pore structure becomes more complex. These changes are helpful to improve the compactness and strength of the materials, thereby improving the gas extraction efficiency.
### Experimental Methods
In the research, nano - silica, sodium silicate, styrene - acrylic emulsion and polycarboxylate superplasticizer were used to prepare low - porosity drilling sealing materials. The influence of porosity on the sealing performance of materials was studied by experimental methods such as liquid nitrogen adsorption and scanning electron microscopy. The experiment was divided into four groups, and the water - cement ratio of each group of materials was 0.45, and the addition amount of polycarboxylate superplasticizer was 1%. Different proportions of nano - silica, sodium silicate and styrene - acrylic emulsion were added to different groups respectively.
### Results and Discussion
The experimental results show that the pore volume of the modified materials is significantly reduced and the proportion of micropores is increased. Specifically:
- The total pore volume of ordinary cement - based sealing materials is 0.09418 cc/g, and the proportion of micropores is 4.56%.
- After adding nano - silica, the pore volume of the material is reduced to 0.08441 cc/g, and the proportion of micropores is increased to 6.64%.
- After adding nano - silica and styrene - acrylic emulsion, the pore volume of the material is further reduced to 0.05621 cc/g, and the proportion of micropores is increased to 16.67%.
In addition, fractal dimension analysis shows that the pore surface roughness of the modified materials is increased and the pore structure becomes more complex. This is helpful to improve the compactness and strength of the materials, thereby improving the gas extraction efficiency.
### Conclusion
This research has successfully optimized the pore structure and strength of drilling sealing materials by adding nano - silica, sodium silicate and styrene - acrylic emulsion. The application of these modified materials is of great significance for improving the extraction efficiency of coal mine gas.