Abstract:The quality of borehole sealing is a key factor affecting the efficiency of gas production. A new water-rich grouting material (RW) with composite coagulant and other additives was prepared in this study to overcome the disadvantages of long setting time and low stone rate of traditional cement materials. When the coagulants A is 4 g and coagulants B is 2 g, the setting time of RW material was reduced by 60.85% and 50.62%, which significantly shortened the setting time of the RW material, respectively. Based on the orthogonal method, 29 groups of comparative experiments were designed to investigate the interaction mechanism between different additives on the performance index of RW, including setting time, water secretion rate, and compressive strength. Quadratic regression equations were fitted using the response surface method. All the correlation coefficients R2 of each response model were greater than 0.97, R2 and R2adj were less than 0.2 through variance analysis, indicating a high correlation between the actual and prediction results. The water–cement ratio had the most significant effect among all factors on setting time, water secretion rate, and compressive strength of the RW material. The scanning electron microscope (SEM) was used to compared the micromorphological characteristics of RW and conventional Portland cement material (PC). The results showed that the hydration products of RW were mostly smack ettringite, calcium silicate hydrate gel, and calcium hydroxide, which interweaved with each other to form a network structure that was denser than the PC material. Furthermore, the interface bonding degree between RW and injected coal was tighter than that of PC, without obvious cracks at the slurry–coal interface. The results indicate that the addition of composite coagulant can significantly accelerate the hydration process of RW material and also enhance the interface strength of injected coal, which is conducive to improving the grouting quality and sealing effect of the extraction borehole.

Preparation of a New Borehole Sealing Material of Coal Seam Water Infusion

Experimental Research on Performance of New Gas Drainage Borehole Sealing Material with High Fluidity

Development and Application of Water Sealing Technology for Gas Drainage Boreholes

Experimental Study on the Optimization of Polymer-Modified Cement-Based Composite Sealing Materials and Mechanical Properties and Permeability of Cemented Coal Bodies

Performance of New Inorganic Retarding Sealing Material for Gas Drainage Boreholes

Study on Performance Optimization of Water-Rich Grouting Materials Based on Response Surface Methodology

Experimental study comparing the microscopic properties of a new borehole sealing material with ordinary cement grout

Research on the Performance of Cement-Based Composite Borehole Sealing Material Based on Orthogonal Test

Comparative analysis of sealing effect of different hole sealing processes in coal mine

Study on the Interaction between Low-Viscosity High-Permeability Pregrouting Sealing Material and Coal and Its Application

Effect of optimized pore structure on sealing performance of drilling sealing materials in coal mine

Study on the mechanical properties and microstructure of a rich-watered grouting material

Development and performance testing of the new sealing material for gas drainage drilling in coal mine

Study on the Mechanics and Pore Characteristics of Coal Seam Drilling Sealing Materials Based on Nanomaterial Optimization.

Microscopic properties and sealing performance of new gas drainage drilling sealing material

Development and performance optimization of a new composite sealing material prepared by drilling cuttings

Parameter Optimization of Constant Pressure Grouting Technology for Borehole Sealing with Inorganic Noncondensable Material in Tectonic Coalbed of South China

Research Progress and Discussion on Modified Cement-Based Borehole Sealing Materials for Mining

Research and application of hydraulic fracturing borehole bag sealing technology

Synergetic Effect Of Ternary Mixture Of Nano Silicon Carbide-Polyvinyl Alcohol-Lithium Sulfate On Early Strength Of Cement

Performance and application of new inorganic retarding sealing material suitable for multi-scale fractures