Solid-State Phase Transformations Involving (Nb,Mo)2CrB2 Borides and (Nb,Ti)2CS Carbosulfides at the Grain Boundaries of Superalloy Inconel 718

S. Vernier,A. Pugliara,B. Viguier,E. Andrieu,L. Laffont
DOI: https://doi.org/10.1007/s11661-020-06045-z
2020-10-14
Metallurgical and Materials Transactions A
Abstract:The present paper studied the solid-state phase transformations occurring at the grain boundaries of a conventional cast-and-wrought alloy within the chemical specifications of superalloy Inconel 718. These phase transformations involved the precipitation of (Nb,Mo)<sub>2</sub>CrB<sub>2</sub> borides and (Nb,Ti)<sub>2</sub>CS carbosulfides, which are usually phases rather associated to solidification phenomena than to solid-state phase precipitation in superalloy Inconel 718. The study started from a material solution-treated above the <i>δ</i> solvus. When this material was heated subsolvus <i>δ</i> from room temperature, (Nb,Mo)<sub>2</sub>CrB<sub>2</sub> borides was found to precipitate at the grain boundaries, in addition to the <i>δ</i> phase. Then, when the material was reheated supersolvus <i>δ</i> after the subsolvus treatment, the complete dissolution of the <i>δ</i> phase and the partial dissolution of the (Nb,Mo)<sub>2</sub>CrB<sub>2</sub> phase released niobium and titanium atoms in the grain boundaries. Both elements have a strong affinity with carbon and sulfur, and this favored the precipitation of secondary (Nb,Ti)C carbides and (Nb,Ti)<sub>2</sub>CS carbosulfides at grain boundaries. An analysis of the interactions between the segregating species C, B and S evidenced that the precipitation of (Nb,Mo)<sub>2</sub>CrB<sub>2</sub> borides at grain boundaries was very likely made possible by a decreased carbon activity during the subsolvus <i>δ</i> treatment.
What problem does this paper attempt to address?