Grain boundary precipitation behavior in Re-containing nickel-based directionally solidified superalloys with carbon and boron additions

Xiao-juan Wang,Lin Liu,Tai-wen Huang,Wen-chao Yang,Quan-zhao Yue,Chuang He,Jun Zhang,Heng-zhi Fu

DOI: https://doi.org/10.1016/j.vacuum.2020.109483

IF: 4

2020-09-01

Vacuum

Abstract:<p>The grain boundary precipitation behavior in Re-containing nickel-based directionally solidified (DS) superalloys with carbon and boron additions were investigated using high-resolution scanning electronic microscopy and transmission electron microscopy. The results indicated that the grain boundary became more tortuous as the carbon and boron contents increased. When the carbon content increased from 0 to 0.130 wt%, the average size and area fraction of the intergranular and intragranular precipitations increased. Similarly, as the boron content increased from 0 to 0.014 wt%, the average size and area fraction of the intragranular precipitation also increased; however, the average size and area fraction of the intergranular precipitation decreased. Furthermore, it was quantitatively estimated that these precipitations preferentially occurred on the grain boundaries at low carbon (&lt;0.040 wt%) and boron (&lt;0.005 wt%) contents; the increases in the carbon (≥0.085 wt%) and boron (≥0.010 wt%) contents promoted the transformation from the intergranular to the intragranular precipitation. During heat treatment, the carbides were mainly of the MC and M₂₃C₆ types, whereas no borides were identified. It was also confirmed that the M₂₃C₆ carbides contained Re, whereas no Re was detected in the MC carbides.</p>

materials science, multidisciplinary,physics, applied