Continuous hot corrosion behaviour of an FeCrAlSi coating prepared by laser cladding
Yixin Yang,Yuxin Li,Zhiguo Liang,Peikang Bai,Jinhao Nie,Siyuan Liu,Bowen Chen,Shouzheng Wei,Qingfeng Guan,Jie Cai
DOI: https://doi.org/10.1016/j.surfcoat.2021.127424
IF: 4.865
2021-09-01
Surface and Coatings Technology
Abstract:<p>FeCrAlSi coatings were prepared using laser cladding technology and subjected to a continuous hot corrosion test in a eutectic 75 wt.% Na<sub>2</sub>SO<sub>4</sub> + 25 wt.% K<sub>2</sub>SO<sub>4</sub> salt at 800°C in air. The FeCrAlSi coating consists of mainly the Fe-Cr solid solution, AlFe intermetallic compound and little FeAl<sub>2</sub> phase, and the microhardness and tribological properties improved over those of the untreated substrate. In the earliest stage of hot corrosion, a protective Al<sub>2</sub>O<sub>3</sub> film is formed. During the subsequent hot corrosion process, the O<sup>2-</sup> concentration gradually increases. The alkalinity of the molten salt/coating interface then increases to the level at which it reacts with Al<sub>2</sub>O<sub>3</sub>, and the newly formed porous Al<sub>2</sub>O<sub>3</sub> film is less protective. In the mid-stage of hot corrosion, Cr continues to diffuse upward through the porous Al<sub>2</sub>O<sub>3</sub> film, and petal-like Cr<sub>2</sub>O<sub>3</sub> forms on the pores, gradually forming a continuous Cr<sub>2</sub>O<sub>3</sub> film. In the subsequent hot corrosion process, the internal oxidation of the Al intensifies, and the phenomenon of Al<sub>2</sub>O<sub>3</sub> phase diffusing into the interior is more obvious. In the last stage of hot corrosion, the SiO<sub>2</sub> film exists in the internal corrosion layer, which is passivated in the molten sulphate. Additionally, Al<sub>2</sub>O<sub>3</sub> no longer penetrates the coating, thus forming a protective oxidation film with the (Cr, Fe)<sub>2</sub>O<sub>3</sub> + Al<sub>2</sub>O<sub>3</sub> in the external corrosion layer, which effectively slows oxidation and sulphuration reactions.</p>
physics, applied,materials science, coatings & films