The study of mechanical properties and corrosion behavior of the Fe-based amorphous alloy coatings using high velocity oxygen fuel spraying

Tzu-Jing Lin,Hung-Hua Sheu,Chun-Ying Lee,Hung-Bin Lee

DOI: https://doi.org/10.1016/j.jallcom.2021.159132

IF: 6.2

2021-06-01

Journal of Alloys and Compounds

Abstract:<p>The Fe-based amorphous alloy powders Fe₄₀-Cr₁₉-Mo₁₈-C₁₅-B₈ are sprayed on 316 stainless steel substrates by high velocity oxygen fuel spraying (HVOF) process. The microstructure of coatings are analyzed by XRD, SEM, XPS and TEM. The corrosion behavior of coatings under different corrosive solutions is also studied. The experimental results presented that the average hardness of coating is approximately at 1024 Hv, contact angle is from 72° to 74°. The scratch test result shows that the LC₂ value of coatings occurred at 46.0 N. SEM images presented that there are micro-holes and micro-cracks in coatings. XRD pattern and TEM images indicated the microstructure of coatings are the amorphous structure and amorphous/crystalline mixed structure. The potentiodynamic polarization analysis results show the corrosion resistance of coatings under sea water and 3.5 wt% NaCl solution has a transition behaviors of activation, passivation and over passivation. Through the cold and heat alternating salt spray corrosion test and the high-speed water erosion test, the surface of coatings rusted after 12 weeks. The surface of coatings formed passivation film during corrosion test, and it has a very slight weight loss. It can be seen that the Fe-based amorphous alloy has a good stable passivation and a corrosion-resistant.</p>

materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering

What problem does this paper attempt to address?

This paper aims to study the mechanical properties and corrosion behavior of iron - based amorphous alloy coatings prepared by high - velocity oxygen - fuel spraying (HVOF) technology. Specifically, the paper focuses on the following issues:

1. **Mechanical Properties**:
- Research on mechanical properties such as hardness, contact angle and adhesion of iron - based amorphous alloy coatings.
- Through experimental tests, evaluate the mechanical strength and wear resistance of these coatings under different conditions.

2. **Corrosion Behavior**:
- Analyze the corrosion behavior of iron - based amorphous alloy coatings in different corrosion solutions, including seawater and 3.5 wt% NaCl solution.
- Evaluate the corrosion current density and corrosion potential of the coatings through electrochemical tests (such as potentiodynamic polarization curves and open - circuit potential tests).
- Observe the surface changes and weight loss of the coatings in the alternating hot - cold salt - spray corrosion test and high - speed water - flow erosion test to evaluate their long - term corrosion resistance.

3. **Microstructure**:
- Use techniques such as X - ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and X - ray photoelectron spectroscopy (XPS) to analyze the microstructure and chemical composition of the coatings.
- Research on the microstructure changes of the coatings during the corrosion process, especially the formation and propagation of micro - cracks, and the formation mechanism of the oxide film.

4. **Corrosion Mechanism**:
- Explore the corrosion mechanism of iron - based amorphous alloy coatings in different corrosion environments, especially the corrosion behavior after long - term exposure in the marine environment.
- Through XPS analysis, study the changes in the oxidation states of elements during the corrosion process, especially the changes in the oxidation states of iron, chromium and molybdenum.

In summary, this paper mainly solves the key problems of iron - based amorphous alloy coatings in terms of mechanical properties and corrosion behavior, providing an important scientific basis for performance optimization in practical applications.