Continuous hot corrosion behaviour of an FeCrAlSi coating prepared by laser cladding

Yixin Yang,Yuxin Li,Zhiguo Liang,Peikang Bai,Jinhao Nie,Siyuan Liu,Bowen Chen,Shouzheng Wei,Qingfeng Guan,Jie Cai

DOI: https://doi.org/10.1016/j.surfcoat.2021.127424

IF: 4.865

2021-09-01

Surface and Coatings Technology

Abstract:<p>FeCrAlSi coatings were prepared using laser cladding technology and subjected to a continuous hot corrosion test in a eutectic 75 wt.% Na₂SO₄ + 25 wt.% K₂SO₄ salt at 800°C in air. The FeCrAlSi coating consists of mainly the Fe-Cr solid solution, AlFe intermetallic compound and little FeAl₂ phase, and the microhardness and tribological properties improved over those of the untreated substrate. In the earliest stage of hot corrosion, a protective Al₂O₃ film is formed. During the subsequent hot corrosion process, the O^2- concentration gradually increases. The alkalinity of the molten salt/coating interface then increases to the level at which it reacts with Al₂O₃, and the newly formed porous Al₂O₃ film is less protective. In the mid-stage of hot corrosion, Cr continues to diffuse upward through the porous Al₂O₃ film, and petal-like Cr₂O₃ forms on the pores, gradually forming a continuous Cr₂O₃ film. In the subsequent hot corrosion process, the internal oxidation of the Al intensifies, and the phenomenon of Al₂O₃ phase diffusing into the interior is more obvious. In the last stage of hot corrosion, the SiO₂ film exists in the internal corrosion layer, which is passivated in the molten sulphate. Additionally, Al₂O₃ no longer penetrates the coating, thus forming a protective oxidation film with the (Cr, Fe)₂O₃ + Al₂O₃ in the external corrosion layer, which effectively slows oxidation and sulphuration reactions.</p>

physics, applied,materials science, coatings & films