Thermal Stability and Hot Corrosion Performance of the AlCoCrFeNi2.1 High-Entropy Alloy Coating by Laser Cladding

Li Zhang,Yan Ji,Bin Yang
DOI: https://doi.org/10.3390/ma16175747
IF: 3.4
2023-08-23
Materials
Abstract:Both crack-free AlCoCrFeNi2.1 eutectic high-entropy alloy (EHEA) and Y and Hf co-doping AlCoCrFeNi2.1 EHEA (YHf-EHEA) coatings were prepared by laser cladding. The solidification microstructure, thermal stability, and hot corrosion performance of the coatings at 900 °C under 75% Na2SO4 + 25% NaCl molten salts were investigated. The experimental results showed that the structure of the as-deposited coatings consisted of FCC and BCC/B2 phases. After heat treatment, an Al-rich L12 phase was precipitated in the FCC phase of all coatings. The grain sizes of the EHEA and YHf-EHEA coatings after heat treatment at 900 °C for 10 h increased by 27.5% and 15.7%, respectively, compared to the as-deposited coatings. Meanwhile, after hot corrosion, the spallation areas of the YHf-EHEA and EHEA coatings accounted for 14.98% and 5.67% of the total surface area, respectively. In this study, the Y and Hf co-doping did not change the microstructure morphology and phase structure of the coatings but did improve the thermal stability and resistance of the hot corrosion oxide scale spallation, providing a certain amount of data and theoretical support for the application of EHEA coatings as high-temperature protective coatings.
materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,metallurgy & metallurgical engineering
What problem does this paper attempt to address?
The paper aims to address the issues of thermal stability and thermal corrosion performance of materials in high-temperature environments, particularly for protective coatings in harsh conditions such as steam pipelines and the front-end components of gas turbines. Specifically, the study prepared two types of high-entropy alloy (HEA) coatings using laser cladding technology: one is the AlCoCrFeNi 2.1 eutectic high-entropy alloy (EHEA), and the other is the EHEA coating with added yttrium (Y) and hafnium (Hf) elements (YHf-EHEA). The main objective of the research is to investigate the thermal stability and thermal corrosion resistance of these coatings at 900°C in a mixed molten salt environment of 75% sodium sulfate (Na₂SO₄) and 25% sodium chloride (NaCl). The study found that both coatings exhibited certain phase structure changes after heat treatment. Notably, the co-doping of Y and Hf did not alter the basic microstructure and phase composition of the coatings but significantly improved their thermal stability and resistance to thermal corrosion oxide scale spalling. Therefore, this research provides data support and theoretical basis for the application of EHEA coatings as high-temperature protective coatings.