Abstract:The anisotropic fracture behavior of cold-drawn pearlitic steels was analyzed up to a true strain of 1.6. The structures were analyzed and quantified by scanning electron microscopy, electron backscatter diffraction and high-resolution electron microscopy. The aspect ratio Λ was defined to describe the fracture mechanism based on statistics pertaining to major axis and minor axis of pearlitic colonies, and the fitting formula was established as follows: Λ=0.4exp(2x)+0.65. At Λ ≤ 2.75, the fracture mechanism shifts from cleavage to quasi-cleavage fracture due to dislocation generation, as the measured parameters of interlamellar spacing (ILS) showed no obvious decrease. At values of Λ > 2.75, ductile fracture mechanism becomes dominant due to a drastic decrease in ILS. The <110> ferrite fiber microtexture formed during the cold drawing process and the component exhibiting a gradient distribution from the surface to the central regions increased gradually with drawing. The crack propagation path was then deflected and formed a ‘V’ shape at ε ≤ 1.5. However, as carbon migrated from cementite to the ferrite near the interphase, the fracture path deflected again. Furthermore, two reasonable models were formulated to explain fracture crack forming and anisotropic fracture behavior. In addition, this study illustrated that the relative crystallographic orientation of the ferrite and cementite components followed the Bagarytski relationship. With increasing strain, the cementite layers transformed from single crystals into nanostructured polycrystals and even evolved an amorphous structure at the interface at strains above 1.5.

Effect of Strain Aging on Stages of Plastic Strain and Tensile Fracture of Specimens of Steel 08G2B. Part I. Yield Plateau and the Stage of Strain Hardening

Multi-scale Deformation Behavior Investigation of 18cr–8ni Austenitic Steel Subjected to Low-Cycle Fatigue Loading

Aging-dependent Strain Localization in Amorphous Glassy Polymers: from Necking to Shear Banding

The low-cycle fatigue, deformation and final fracture behaviour of an austenitic stainless steel

Changes in the Stress–Strain States of Subsurface Layers of Steel During Loading

Effects of Dynamic Strain Aging on Strain Hardening Behavior, Dislocation Substructure, and Fracture Morphology in a Ferritic Stainless Steel

Characterization of Low Cycle Fatigue of Ferritic–Martensitic P92 Steel: Effect of Temperature

Postponing the Fracture Strain of Ultrafine-Grained 316LN Steel by Sequential Activations of Deformation Modes at 77 K

Influence of Deformation on the Structural–Phase State of Structural Steel and on the Formation of Its Yield Strength and Degree of Hardening

Deformation Stages of Austenitic Cast SteeL 60Cr24NMn16 Under Different Boundary Loading Conditions

Optical Strain Measurement and Microfractography of the Fractures of Armstal 550 Steel after Temperature Tensile Tests

Dislocation Structure in a Strain Localization Band Formed in Normalized 09G2S Steel under Tension

Factors Affecting Kinetics of Strain Aging in S275JRC Steel

Effect of Strain-Hardening on the Length of Plastic Zone of Steel Frames

Effects of Mechanical Deformation on Dislocation Density and Phase Partitioning in 4130 Steel

Effect of long-term aging on the low cycle fatigue behavior and microstructure of a 10% Cr martensitic steel with low nitrogen and high boron contents at 650 °C

Analysis of hardening mechanisms of rail steel under plastic deformation by uniaxial compression

Damage accumulation in carbon steel under low-cycle loading at the crack initiation stage and strain ageing temperature

Microstructural Dependence of Anisotropic Fracture Mechanisms in Cold-Drawn Pearlitic Steels

High-Temperature Low-Cycle Fatigue Behavior of HS80H Ferritic–Martensitic Steel Under Dynamic Strain Aging

Strain-Hardening Behavior of Dual-Phase Steel under Multistress States