Abstract:Magnesium (Mg) alloys have promising potentials for lightweight and biomedical applications. Although there has been a recent interest in producing Mg alloys (including AZ, ZK and WE series) using additive manufacturing (AM), the process-structure-corrosion properties relationships in AM Mg alloys are yet to be understood. Herein, the production of Mg alloy WE43 was achieved by selective laser melting (SLM). The alloy was investigated after SLM, hot isostatic pressing (HIP) as well as an additional solutionising heat treatment. Specimens were carefully characterised, whilst assessed and contrast relative to the conventionally cast alloy counterpart. Characterisation included detailed microstructural analysis employing analytical transmission electron microscopy, X-ray mapping, and electron backscatter diffraction, which revealed the SLM prepared specimens possess a unique microstructure comprising fine grains growing with a strong [0001] texture along the building direction. The SLM prepared specimens also revealed a low fraction of process-induced and metallurgical defects, reaching < 0.1% after optimising the SLM parameters and HIP treatment. The SLM prepared WE43 was found to be cathodically more active relative to the cast WE43 because of a fine distribution of zirconium-, yttrium- and oxygen-rich particles as well as the alterations in the chemical composition of the solid-solution matrix originating from the high cooling rates of SLM. It was revealed that the oxide particles were mainly sourced by powder and thus it is hypothesised that the corrosion of SLM prepared Mg alloys could be greatly improved once the influence of powder characteristics is further understood and controlled.

Research on the formation process of selective laser melting Mg–Y–Sm–Zn–Zr alloy

Microstructure and Mechanical Properties of Selective Laser Melted Mg-9 Wt%al Powder Mixture

Formability, Microstructure, and Thermal Crack Characteristics of Selective Laser Melting of ZK60 Magnesium Alloy

Fabrication of High-Strength Mg-Gd-Zn-Zr Alloy Via Selective Laser Melting

Effect of process parameters on the densification of SLM-produced Mg–Y–Sm–Zn–Zr alloy

Microstructure and mechanical properties of high strength Mg−15Gd−1Zn−0.4Zr alloy additive-manufactured by selective laser melting process

Selective Laser Melting of Mg-Zn Binary Alloys: Effects of Zn Content on Densification Behavior, Microstructure, and Mechanical Property

Selective Laser Melting of Al-Cu-Mn-Mg Alloys: Processing and Mechanical Properties

A Study on Sc- and Zr-modified Al–Mg Alloys Processed by Selective Laser Melting

Effect of Al3(Sc, Zr) and Mg2Si Precipitates on Microstructure and Tensile Properties of Selective Laser Melted Al-14.1Mg-0.47Si-0.31Sc-0.17Zr Alloy

Tensile property and microstructure of Al−4.77Mn−1.37Mg−0.67Sc−0.25Zr alloy under different selective laser melting processing parameters

Selective Laser Melting of Gas Atomized Al–3.02Mg–0.2Sc–0.1Zr Alloy Powder: Microstructure and Mechanical Properties

Study on microstructure and properties of selective laser melting formed AlSi10Mg alloy

Microstructure and Mechanical Properties of an Er-Modified Al–Mg–Mn–Sc–Zr Alloy Processed by Selective Laser Melting

A detailed microstructural and corrosion analysis of an additively manufactured magnesium alloy produced by selective laser melting

Selective laser melting of Al-3.48Cu-2.03Si-0.48Sc-0.28Zr alloy: Microstructure evolution, properties and metallurgical defects

Effects of magnesium on microstructure, properties and degradation behaviors of zinc-based alloys prepared by selective laser melting

Effect of laser power on microstructures and properties of Al-4.82Mg-0.75Sc-0.49Mn-0.28Zr alloy fabricated by selective laser melting

Research progress on selective laser melting (SLM) of magnesium alloys: A review

Achieving Ultra-High Strength and Ductility in Mg–9Al–1Zn–0.5Mn Alloy Via Selective Laser Melting

Microstructure and mechanical properties of Al-Fe-Sc-Zr alloy additively manufactured by selective laser melting