Abstract:The laser power and scan speed are significant processing parameters influencing the defects and microstructures due to affecting the thermal state within the melt pool during laser powder bed fusion (LPBF). To this end, these process parameter combinations under a constant laser energy density are correlated with defects (balling phenomenon and pores) and microstructures (melt pool arrangement and cell morphology). Setting the parameter combination (laser power and scan speed are 200 W and 910 mm/s, respectively) yields large balling droplets (average size of 150 μm) due to the relatively high melt viscosity resulting from the low melt pool temperature. In this case, a limited surface tension difference acting on a liquid surface cannot provide sufficient driving forces against viscous drags to promote the efficient spreading of the molten alloy. Cavity regions are formed between the large balling droplets and the previous layer, forming lack-of -fusion pores. By increasing the laser power and scan speed gradually, samples with relative densities greater than 99.5% are produced. This phenomenon can be attributed to the increases in laser power and scan speed, which improves the spreading ability of the molten alloy. With increasing laser power and scan speed, the cell size decreases (from 0.51 μm to 0.42 μm) because of the increase in the cooling rate. The sample (laser power and scan speed are 350 W and 1590 mm/s, respectively) has the highest performance (310 MPa yield strength, 470 MPa ultimate tensile strength, and 6.6% fracture strain) due to its highest relative density (greater than 99.5%) and fine microstructure (average cell size of 0.45 μm). All four samples exhibit anisotropic mechanical properties resulting from the combination of the melt pool boundary and lack-of-fusion pores.

Effect of process parameters on the densification of SLM-produced Mg–Y–Sm–Zn–Zr alloy

Selective laser melting of CuCrZr alloy: processing optimisation, microstructure and mechanical properties

Effect of Processing Parameters on Tensile Properties and Microstructure of Selective Laser Melted AlSi10Mg Alloy

Microstructure and Mechanical Properties of Selective Laser Melted Mg-9 Wt%al Powder Mixture

Selective Laser Melting of Mg-Zn Binary Alloys: Effects of Zn Content on Densification Behavior, Microstructure, and Mechanical Property

Densification, microstructure and properties of Sc and Zr modified Al-Mn alloy prepared by selective laser melting

The AlSi10Mg Samples Produced by Selective Laser Melting: Single Track, Densification, Microstructure and Mechanical Behavior

Experimental Research on Selective Laser Melting AlSi10Mg Alloys: Process, Densification and Performance

Tensile property and microstructure of Al−4.77Mn−1.37Mg−0.67Sc−0.25Zr alloy under different selective laser melting processing parameters

Selective Laser Melting of Al-Cu-Mn-Mg Alloys: Processing and Mechanical Properties

Processing defect, microstructure evolution and mechanical properties of laser powder bed fusion Al-12Si alloys

Research on the formation process of selective laser melting Mg–Y–Sm–Zn–Zr alloy

Effects of processing parameters on fabrication defects, microstructure and mechanical properties of additive manufactured Mg–Nd–Zn–Zr alloy by selective laser melting process

Effect of process parameters on microstructures and properties of Al-42Si alloy fabricated by selective laser melting

Process parameter optimization for selective laser melting Ti-6Al-4V with high layer thickness

The effect of process parameters on the physical and mechanical properties of Ti fabricated by selective laser melting using ball milled powders

Microstructure, metallurgical defects and hardness of Al–Cu–Mg–Li–Zr alloy additively manufactured by selective laser melting

Selective laser melting of Al-3.48Cu-2.03Si-0.48Sc-0.28Zr alloy: Microstructure evolution, properties and metallurgical defects

Cracking Behavior, Microstructure and Properties of Selective Laser Melted Al-Mn-Mg-Sc-Zr Alloy

Effects of process parameters on the microstructure and mechanical properties of 24CrNiMo steel fabricated by selective laser melting

Mechanical Properties of High Mg-Content Al-Mg-Sc-Zr Alloy Fabricated by Selective Laser Melting