Influence Factors and Preparation Conditions of Ni/AC Used as A Low-temperature Desulfurizer
HUANG Bangfu,GENG Chaoyang,SHI Zhe,DING Yuehua,ZHANG Guifang,ZHOU Xiaolei,LIU Lanpeng
DOI: https://doi.org/10.16258/j.cnki.1674-5906.2018.01.015
2018-01-01
Abstract:Activated carbon (AC)-loaded nickel (Ni) exhibits good low-temperature desulfurization performance. In this study, coconut husk AC was the object under investigation, with the aim of developing AC for the low-temperature desulfurization of iron-steel sintering flue gas. Ni/AC was prepared using the nickel nitrate immersion method. By simulating sintering flue gas, the desulfurization performances of AC and Ni/AC (0.5%, 1%, 2%, 3% and 4%, marking as 0.5Ni/AC, 1Ni/AC, 2Ni/AC, 3Ni/AC and 4Ni/AC, respectively) were analyzed by conducting a desulfurization experiment. The surface properties of AC and Ni/AC were observed by SEM and X-rays. The AC desulfurization test results were as follows: the reaction temperature at 30°C exhibited good desulfurization performance, the low reaction temperature was propitious to physical adsorption, the high reaction temperature was propitious to chemical adsorption, and the desulphurization mechanism involved AC absorbing SO2, O2, and H2O, then, adsorbates turned into sulfuric acid under millipore conditions. The desulfurizer influence factors of reaction temperature, airspeed, and SO2 mass fractions of entrance were investigated by conducting a 1Ni/AC desulfurization experiment. The characterization results revealed the following: the reaction temperature at 60 ℃ exhibited good desulfurization performance, the endurance time of 100% desulfurization ratio could be maintained for 120 min, the low airspeed was propitious to desulfurization, and the SO2mass fractions of entrance between 0.1% and 0.3% was propitious to desulfurization. By analyzing the characterization results, we observed that there were many desulfurization products that existed on the pore surface. The desulfurization products jammed the pore path and covered the active site. Finally, the reaction chain of desulfurization was cut off. When the sintering temperature was higher than 900 ℃, the nickel was a simple substance . When the sintering temperature was between 600 ℃ and 800 ℃, the catalyst had a high desulfurization ratio, and the nickel turned into NiO. Then, the Ni load quantity equaled 1% and the AC exhibited better low-temperature desulfurization performance. These research findings can aid in low-temperature desulfurization and the simultaneous control of multiple pollutants for iron-steel sintering flue gas.